Rust

Rust
Colors of rust

Rust is a general term for a series of iron oxides. In colloquial usage, the term is applied to red oxides, formed by the reaction of iron and oxygen in the presence of water or air moisture. There are also other forms of rust, such as the result of the reaction of iron and chlorine in an environment deprived of oxygen, such as rebar used in underwater concrete pillars, which generates green rust. Several forms of rust are distinguishable visually and by spectroscopy, and form under different circumstances.[1] Rust consists of hydrated iron(III) oxides Fe2O3·nH2O and iron(III) oxide-hydroxide (FeO(OH), Fe(OH)3). Given sufficient time, oxygen, and water, any iron mass will eventually convert entirely to rust and disintegrate. Surface rust provides no protection to the underlying iron, unlike the formation of patina on copper surfaces.

Rusting is the common term for corrosion of iron and its alloys, such as steel. Many other metals undergo equivalent corrosion, but the resulting oxides are not commonly called rust.

Contents

Chemical reactions

Heavy rust on the links of a chain near the Golden Gate bridge in San Francisco; it was continuously exposed to moisture and salt-laden spray, causing surface breakdown, cracking, and flaking of the metal.

Oxidation of iron metal

When impure(cast) iron is in contact with water, oxygen, or other strong oxidants and/or acids, it rusts. If salt is present as, for example, in salt water, it tends to rust more quickly, as a result of the electro-chemical reactions. Iron metal is relatively unaffected by pure water or by dry oxygen. As with other metals, like aluminium, a tightly adhering oxide coating, a passivation layer, protects the bulk iron from further oxidation. Thus, the conversion of the passivating iron oxide layer to rust results from the combined action of two agents, usually oxygen and water. Other degrading solutions are sulfur dioxide in water and carbon dioxide in water. Under these corrosive conditions, iron hydroxide species are formed. Unlike iron oxides, the hydroxides do not adhere to the bulk metal. As they form and flake off from the surface, fresh iron is exposed, and the corrosion process continues until either all of the iron is consumed or all of the oxygen, water, carbon dioxide, or sulfur dioxide in the system are removed or consumed.[2]

Associated reactions

A rusted (and dirt-encrusted) bolt; note the surface pitting and gradual shape-deformation, caused by severe oxidation
Rust in pipes can result in brown and black water.

The rusting of iron is an electrochemical process that begins with the transfer of electrons from iron to oxygen.[3] The rate of corrosion is affected by water and accelerated by electrolytes, as illustrated by the effects of road salt on the corrosion of automobiles. The key reaction is the reduction of oxygen:

O2 + 4 e- + 2 H2O → 4 OH-

Because it forms hydroxide ions, this process is strongly affected by the presence of acid. Indeed, the corrosion of most metals by oxygen is accelerated at low pH. Providing the electrons for the above reaction is the oxidation of iron that may be described as follows:

Fe → Fe2+ + 2 e

The following redox reaction also occurs in the presence of water and is crucial to the formation of rust:

4 Fe2+ + O2 → 4 Fe3+ + 2 O2−

In addition, the following multistep acid-base reactions affect the course of rust formation:

Fe2+ + 2 H2O Fe(OH)2 + 2 H+
Fe3+ + 3 H2O Fe(OH)3 + 3 H+

as do the following dehydration equilibria:

Fe(OH)2 FeO + H2O
Fe(OH)3 FeO(OH) + H2O
2 FeO(OH) Fe2O3 + H2O
Rusted pyrite cubes

From the above equations, it is also seen that the corrosion products are dictated by the availability of water and oxygen. With limited dissolved oxygen, iron(II)-containing materials are favoured, including FeO and black lodestone (Fe3O4). High oxygen concentrations favour ferric materials with the nominal formulae Fe(OH)3-xOx/2. The nature of rust changes with time, reflecting the slow rates of the reactions of solids.

Furthermore, these complex processes are affected by the presence of other ions, such as Ca2+, both of which serve as an electrolyte, and thus accelerate rust formation, or combine with the hydroxides and oxides of iron to precipitate a variety of Ca-Fe-O-OH species.

What's more, rust indicator can be used for testing the presence of Fe2+. Fe2+ turns the rust indicator from yellow to blue.

Prevention

Rust is permeable to air and water, therefore the interior iron continues to corrode. Rust prevention thus requires coatings that preclude rust formation. Stainless steel forms a passivation layer of chromium(III) oxide. Similar passivation behavior occurs with magnesium, titanium, zinc, zinc oxides, aluminium, polyaniline, and other electroactive conductive polymers.

Galvanization

An important approach to rust prevention entails galvanization, which typically consists of an application, on the object to be protected, of a layer of zinc by either hot-dip galvanizing or electroplating. Zinc is traditionally used because it is cheap, adheres well to steel, and provides a cathodic protection to the steel surface in case of damage of the Zinc layer. In more corrosive environments (such as salt water), cadmium is preferred. Galvanization often fails at seams, holes, and joints where the coating is pierced. In these cases, the coating provides cathodic protection to metal, where it acts as a galvanic anode rusting in preference. More modern coatings add aluminium to the coating as zinc-alume; aluminium will migrate to cover scratches and thus provide protection for longer. These approaches rely on the aluminium and zinc oxides protecting the once-scratched surface rather than oxidizing as a sacrificial anode. In some cases, very aggressive environments or long design life, both zinc and a coating are applied to provide corrosion protection.

Cathodic protection

Cathodic protection is a technique used to inhibit corrosion on buried or immersed structures by supplying an electrical charge that suppresses the electro-chemical reaction. If correctly applied, corrosion can be stopped completely. In its simplest form, it is achieved by attaching a sacrificial anode, thereby making the iron or steel the cathode in the cell formed. The sacrificial anode must be made from something with a more negative electrode potential than the iron or steel, commonly zinc, aluminium, or magnesium.

Coatings and painting

Flaking paint, exposing a patch of surface rust on sheet-metal

Rust formation can be controlled with coatings, such as paint, that isolate the iron from the environment. Large structures with enclosed box sections, such as ships and modern automobiles, often have a wax-based product (technically a "slushing oil") injected into these sections (see Rustproofing). Such treatments also contain rust inhibitors. Covering steel with concrete can provide some protection to steel by the high pH environment at the steel-concrete interface. However rusting of steel in concrete can still be a problem.

Plating

Rusting can completely degrade iron. Note the galvanization on the unrusted portions.
  • Zinc plating (galvanized iron/steel): iron or steel coated with zinc metal layer. Hot-dipped method or zinc-blasting method may be used.
  • Tin plating: mild steel sheet coated with a tin layer.
  • Chrome plating: wherein a thin layer of chromium is electrolytically applied to the steel, providing both rust protection and a highly polished, bright appearance. Often used on the silver-coloured components of bicycles, motorbikes, and automobiles.

Bluing

Bluing is a technique that can provide limited resistance to rusting for small steel items, such as firearms; for it to be successful, water-displacing oil is rubbed onto the blued steel.

Humidity

Rust can be avoided by controlling the moisture in the atmosphere. An example of this is the use of silica gel.

Inhibitors

Corrosion inhibitors, like gas-phase or volatile inhibitors, can be used to prevent corrosion in closed systems.

Economic impact

The collapsed Silver Bridge, as seen from the Ohio side

Rust is associated with degradation of iron-based tools and structures. As rust has a much higher volume than the originating mass of iron, its build-up can also cause failure by forcing apart adjacent parts — a phenomenon sometimes known as "rust smacking". It was the cause of the collapse of the Mianus river bridge in 1983, when the bearings rusted internally and pushed one corner of the road slab off its support. Rust was also an important factor in the Silver Bridge disaster of 1967 in West Virginia, when a steel suspension bridge collapsed in less than a minute, killing 46 drivers and passengers on the bridge at the time.

The Kinzua Bridge after it collapsed

Kinzua Bridge in Pennsylvania was blown down by a tornado in 2003 largely because the central base bolts holding the structure to the ground had rusted away, leaving the bridge resting by gravity alone.

Likewise, corrosion of concrete-covered steel and iron can cause the concrete to spall, creating severe structural problems. It is one of the most common failure modes of reinforced concrete bridges.

See also

A blacksmith removing rust with sand prior to welding

References

  1. ^ "Interview, David Des Marais". http://nasa.gov/centers/ames/multimedia/audio/MER/mer13.html. 
  2. ^ Holleman, A. F.; Wiberg, E. "Inorganic Chemistry" Academic Press: San Diego, 2001. ISBN 0-12-352651-5.
  3. ^ Gräfen, H.; Horn, E. M.; Schlecker, H.; Schindler, H. (2000). "Corrosion". Ullmann's Encyclopedia of Industrial Chemistry. Wiley-VCH. doi:10.1002/14356007.b01_08.  edit

External links


Wikimedia Foundation. 2010.

Игры ⚽ Поможем написать курсовую
Synonyms:

Look at other dictionaries:

  • rust — sb., en …   Dansk ordbog

  • Rust — ist der Name folgender Orte: Rust (Burgenland), eine Freistadt (Stadt mit eigenem Statut) im Burgenland, Österreich Rust (Baden), eine Gemeinde im Ortenaukreis, Baden Württemberg, Deutschland Rust im Tullnerfeld, eine Katastralgemeinde der… …   Deutsch Wikipedia

  • rust — /rust/, n. 1. Also called iron rust. the red or orange coating that forms on the surface of iron when exposed to air and moisture, consisting chiefly of ferric hydroxide and ferric oxide formed by oxidation. 2. any film or coating on metal caused …   Universalium

  • Rust — Rust, n. [AS. rust; akin to D. roest, G. & Sw. rost, Icel. ry[eth]; named from its color, and akin to E. red. [root]113. See {Red}.] 1. (Chem.) The reddish yellow coating formed on iron when exposed to moist air, consisting of ferric oxide or… …   The Collaborative International Dictionary of English

  • rust — [rust] n. [ME < OE, akin to Ger rost < IE base * reudh ,RED] 1. the reddish brown or reddish yellow coating formed on iron or steel by oxidation, as during exposure to air and moisture: it consists mainly of ferric oxide, Fe2O3, and ferric… …   English World dictionary

  • Rust — Rust, v. i. [imp. & p. p. {Rusted}; p. pr. & vb. n. {Rusting}.] [AS. rustian.] 1. To contract rust; to be or become oxidized. [1913 Webster] If gold ruste, what shall iron do? Chaucer. [1913 Webster] Our armors now may rust. Dryden. [1913… …   The Collaborative International Dictionary of English

  • Rust — Rust, v. t. 1. To cause to contract rust; to corrode with rust; to affect with rust of any kind. [1913 Webster] Keep up your bright swords, for the dew will rust them. Shak. [1913 Webster] 2. Fig.: To impair by time and inactivity. Johnson. [1913 …   The Collaborative International Dictionary of English

  • Rust — Saltar a navegación, búsqueda Rust Ciudad de Austria Ubicación    • Latitud 47° 48 N …   Wikipedia Español

  • rust — rust; rust·i·ly; rust·i·ness; rust·proof·er; …   English syllables

  • rust — [n] corrosion blight, corruption, decay, decomposition, dilapidation, mold, oxidation, rot, wear; concepts 309,720 rust [v] corrode decay, decline, degenerate, deteriorate, oxidize, stale, tarnish, wither; concept 469 …   New thesaurus

  • rust — ► NOUN 1) a reddish or yellowish brown flaky coating of iron oxide that is formed on iron or steel by oxidation, especially in the presence of moisture. 2) a fungal disease of plants which results in reddish or brownish patches. 3) a reddish… …   English terms dictionary

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”