- Mechanical overload
The failure or fracture of a product or component in a single event is known as mechanical overload. It is a common failure mode, and may be contrasted with fatigue, creep, rupture, or stress relaxation. The terms are used in forensic engineering and structural engineering when analysing product failure. Failure may occur because either the product is weaker than expected owing to a stress concentration, or the applied load is greater than expected and exceeds the normal tensile strength, shear strength or compressive strength of the product.
Materials failure modes
Examples include the many components which fail in car crashes, train crashes, and airplane crashes as a result of impact loading. The problem for the investigator is to determine which failures have been caused by the crash, and which may have caused the crash. It usually involves examining the broken parts for signs of fatigue crack growth or other damage to the part which cannot be attributed to the crash itself. For very large structural failures such as the collapse of bridges, it is necessarily a long and tedious process of sifting the broken parts.
- Strength of Materials, 3rd edition, Krieger Publishing Company, 1976, by Timoshenko S.,ISBN 0-88275-420-3
- Forensic Materials Engineering: Case Studies by Peter Rhys Lewis, Colin Gagg, Ken Reynolds, CRC Press (2004).
Wikimedia Foundation. 2010.
Look at other dictionaries:
Overload — may refer to: Contents 1 Music 1.1 Bands 1.2 Albums 1.3 Songs 2 Medical … Wikipedia
Belt (mechanical) — For other belts, see Belt (disambiguation). A pair of vee belts … Wikipedia
Torque limiter — A torque limiter is an automatic device that protects mechanical equipment, or its work, from damage by mechanical overload. A torque limiter may limit the torque by slipping (as in a friction plate slip clutch), or uncouple the load entirely (as … Wikipedia
Fatigue (material) — Metal fatigue redirects here. For the video game, see Metal Fatigue (disambiguation). v · d · e Materials failure modes … Wikipedia
Wear — For other uses, see Wear (disambiguation). v · d · e Materials failure modes … Wikipedia
Fouling — This article is about fouling in engineering. For uses of the term foul outside technology, see Foul (disambiguation). Not to be confused with fowling. Heat exchanger in a steam power plant, fouled by macro fouling … Wikipedia
Forensic materials engineering — A branch of Forensic engineering, the subject focuses on the material evidence from crime or accident scenes, seeking defects in those materials which might explain why an accident occurred, or the source of a specific material to identify a… … Wikipedia
Charpy impact test — v · d · e Materials failure modes Buckling · … Wikipedia
Metallurgical failure analysis — is the process by which a metallurgist determines the mechanism that has caused a metal component to fail. Typical failure modes involve various types of corrosion and mechanical damage. It has been estimated that the direct annual cost of… … Wikipedia
Corrosion — v · d · e Materials failure modes Buckling · … Wikipedia