 Electron mobility

This article is about the mobility for electrons and holes in metals and semiconductors. For the general concept, see Electrical mobility.
In solidstate physics, the electron mobility characterizes how quickly an electron can move through a metal or semiconductor, when pulled by an electric field. In semiconductors, there is an analogous quantity for holes, called hole mobility. The term carrier mobility refers in general to both electron and hole mobility in semiconductors.
Electron and hole mobility are special cases of electrical mobility of charged particles in a fluid under an applied electric field.
When an electric field E is applied across a piece of material, the electrons respond by moving with an average velocity called the drift velocity, . Then the electron mobility μ is defined as
 .
Electron mobility is almost always specified in units of cm^{2}/(V·s). This is different from the SI unit of mobility, m^{2}/(V·s). They are related by 1m^{2}/(V·s) = 10^{4}cm^{2}/(V·s).
Conductivity is proportional to the product of mobility and carrier concentration. For example, the same conductivity could come from a small number of electrons with high mobility for each, or a large number of electrons with a small mobility for each. For metals, it would not typically matter which of these is the case, most metal electrical behavior depends on conductivity alone. Therefore mobility is relatively unimportant in metal physics. On the other hand, for semiconductors, the behavior of transistors and other devices can be very different depending on whether there are many electrons with low mobility or few electrons with high mobility. Therefore mobility is a very important parameter for semiconductor materials. Almost always, higher mobility leads to better device performance, with other things equal.
Semiconductor mobility depends on the impurity concentrations (including donor and acceptor concentrations), defect concentration, temperature, and electron and hole concentrations. It also depends on the electric field, particularly at high fields when velocity saturation occurs. It can be determined by the Hall effect, or inferred from transistor behavior.
Introduction
Drift velocity in an electric field
Main article: Drift velocityWithout any applied electric field, in a solid, electrons (or, in the case of semiconductors, both electrons and holes) move around randomly. Therefore, on average there will be no overall motion of charge carriers in any particular direction over time.
However, when an electric field is applied, each electron is accelerated by the electric field. If the electron were in a vacuum, it would be accelerated to faster and faster velocities (called ballistic transport). However, in a solid, the electron repeatedly scatters off crystal defects, phonons, impurities, etc. Therefore, it does not accelerate faster and faster; instead it moves with a finite average velocity, called the drift velocity. This net electron motion is usually much slower than the normally occurring random motion.
In a semiconductor the two charge carriers, electrons and holes, will typically have different drift velocities for the same electric field.
Quasiballistic transport is possible in solids if the electrons are accelerated across a very small distance (as small as the mean free path), or for a very short time (as short as the mean free time). In these cases, drift velocity and mobility are not meaningful.
Definition and units
See also: Electrical mobilityThe electron mobility is defined by the equation:
 .
where:
 E is the magnitude of the electric field applied to a material,
 v_{d} is the magnitude of the electron drift velocity (in other words, the electron drift speed) caused by the electric field, and
 µ is the electron mobility.
The hole mobility is defined by the same equation. Both electron and hole mobilities are positive by definition.
Usually, the electron drift velocity in a material is directly proportional to the electric field, which means that the electron mobility is a constant (independent of electric field). When this is not true (for example, in very large electric fields), the mobility depends on the electric field.
The SI unit of velocity is m/s, and the SI unit of electric field is V/m. Therefore the SI unit of mobility is (m/s)/(V/m) = m^{2}/(V·s). However, mobility is much more commonly expressed in cm^{2}/(V·s) = 10^{−4} m^{2}/(V·s).
Mobility is usually a strong function of material impurities and temperature, and is determined empirically, mobility values are typically presented in table or chart form. Mobility is also different for electrons and holes in a given semiconductor.
Relation to conductivity
There is a simple relation between mobility and electrical conductivity. Let n be the number density of electrons, and let μ_{e} be their mobility. In the electric field E, each of these electrons will move with the velocity vector , for a total current density of (where e is the elementary charge). Therefore, the electrical conductivity σ satisfies:^{[1]}
 σ = neμ_{e}.
This formula is valid when the conductivity is due entirely to electrons. In a ptype semiconductor, the conductivity is due to holes instead, but the formula is essentially the same: If p is the density of holes and μ_{h} is the hole mobility, then the conductivity is
 σ = peμ_{h}.
If a semiconductor has both electrons and holes, the total conductivity is^{[1]}
 σ = e(nμ_{e} + pμ_{h}).
Examples
Typical electron mobility for Si at room temperature (300 K) is 1400 cm^{2}/ (V·s) and the hole mobility is around 450 cm^{2}/ (V·s).^{[2]}
Very high mobility has been found in several lowdimensional systems, such as twodimensional electron gases (2DEG) (3,000,000 cm^{2}/(V·s) at low temperature),^{[3]} carbon nanotubes (100,000 cm^{2}/(V·s) at room temperature) ^{[4]} and more recently, graphene (200,000 cm^{2}/ V·s at low temperature).^{[5]} Organic semiconductors (polymer, oligomer) developed thus far have carrier mobilities below 10 cm^{2}/(V·s), and usually much lower.
Electric field dependence and velocity saturation
Main article: Velocity saturationAt low fields, the drift velocity v_{d} is proportional to the electric field E, so mobility μ is constant. This value of μ is called the lowfield mobility.
As the electric field is increased, however, the carrier velocity increases sublinearly and asymptotically towards a maximum possible value, called the saturation velocity v_{sat}. For example, the value of v_{sat} is on the order of 1×10^{7} cm/s for both electrons and holes in Si. It is on the order of 6×10^{6} cm/s for Ge. This velocity is a characteristic of the material and a strong function of doping or impurity levels and temperature. It is one of the key material and semiconductor device properties that determine a device such as a transistor's ultimate limit of speed of response and frequency.
This velocity saturation phenomenon results from a process called optical phonon scattering. At high fields, carriers are accelerated enough to gain sufficient kinetic energy between collisions to emit an optical phonon, and they do so very quickly, before being accelerated once again. The velocity that the electron reaches before emitting a phonon is:
where ω_{phonon(opt.)} is the optical phonon angular frequency and m*is the carrier effective mass in the direction of the electric field. The value of E_{phonon (opt.)} is 0.063 eV for Si and 0.034 eV for GaAs and Ge. The saturation velocity is only onehalf of v_{emit}, because the electron starts at zero velocity and accelerates up to v_{emit} in each cycle.^{[6]} (This is a somewhat oversimplified description.^{[6]})
Velocity saturation is not the only possible highfield behavior. Another is the Gunn effect, where a sufficiently high electric field can causes intervalley electron transfer, which reduces drift velocity. (This is unusual; increasing the electric field almost always increases the drift velocity, or else leaves it unchanged.) The result is negative differential resistance.
In the regime of velocity saturation (or other highfield effects), mobility is a strong function of electric field. This means that mobility is a somewhat less useful concept, compared to simply discussing drift velocity directly.
Relation between scattering and mobility
Recall that by definition, mobility is dependent on the drift velocity. The main factor determining drift velocity (other than effective mass) is scattering time, i.e., how long the carrier is ballistically accelerated by the electric field until it scatters (collides) with something that changes its direction and/or energy. The most important sources of scattering in typical semiconductor materials, discussed below, are ionized impurity scattering and acoustic phonon scattering (also called lattice scattering). In some cases other sources of scattering may be important, such as neutral impurity scattering, optical phonon scattering, surface scattering, and defect scattering.^{[7]}
Elastic scattering means that energy is (almost) conserved during the scattering event. Some elastic scattering processes are scattering from acoustic phonons, impurity scattering, piezoelectric scattering, etc. In acoustic phonon scattering, electrons scatter from state k to k', while emitting or absorbing a phonon of wave vector q. This phenomenon is usually modeled by assuming that lattice vibrations cause small shifts in energy bands. The additional potential causing the scattering process is generated by the deviations of bands due to these small transitions from frozen lattice positions. ^{[8]}
Ionized impurity scattering
Semiconductors are doped with donors and/or acceptors, which are typically ionized, and are thus charged. The Coulombic forces will deflect an electron or hole approaching the ionized impurity. This is known as ionized impurity scattering. The amount of deflection depends on the speed of the carrier and its proximity to the ion. The more heavily a material is doped, the higher the probability that a carrier will collide with an ion in a given time, and the smaller the mean free time between collisions, and the smaller the mobility. When determining the strength of these interactions due to the longrange nature of the Coulomb potential, other impurities and free carriers cause the range of interaction with the carriers to reduce significantly compared to bare Coulomb interaction.
If these scatterers are near the interface, the complexity of the problem increases due to the existence of crystal defects and disorders. Charge trapping centers that scatter free carriers form in many cases due to defects associated with dangling bonds. Scattering happens because after trapping a charge, the defect becomes charged and therefore starts interacting with free carriers. If scattered carriers are in the inversion layer at the interface, the reduced dimensionality of the carriers makes the case differ from the case of bulk impurity scattering as carriers move only in two dimensions. Interfacial roughness also causes shortrange scattering limiting the mobility of quasi twodimensional electrons at the interface. ^{[8]}
Lattice (phonon) scattering
At any temperature above absolute zero, the vibrating atoms create pressure (acoustic) waves in the crystal, which are termed phonons. Like electrons, phonons can be considered to be particles. A phonon can interact (collide) with an electron (or hole) and scatter it. At higher temperature, there are more phonons, therefore increased phonon scattering which tends to reduce mobility.
Piezoelectric scattering
Piezoelectric effect can occur only in compound semiconductor due to their polar nature. It is small in most semiconductors but may lead to local electric fields that cause scattering of carriers by deflecting them, this effect is important mainly at low temperatures where other scattering mechanisms are weak. These electric fields arise from the distortion of the basic unit cell as strain is applied in certain directions in the lattice. ^{[8]}
Surface roughness scattering
Surface roughness scattering caused by interfacial disorder is short range scattering limiting the mobility of quasi twodimensional electrons at the interface. From highresolution transmission electron micrographs, it has been determined that the interface is not abrupt on the atomic level, but actual position of the interfacial plane varies one or two atomic layers along the surface. These variations are random and cause fluctuations of the energy levels at the interface, which then causes scattering. ^{[8]}
Alloy scattering
In compound (alloy) semiconductors, which many thermoelectric materials are, scattering caused by the perturbation of crystal potential due to the random positioning of substituting atom species in a relevant sublattice is known as alloy scattering. This can only happen in ternary or higher alloys as their crystal structure forms by randomly replacing some atoms in one of the cubic lattices (sublattice) that form zincblende structure. Generally, this phenomenon is quite weak but in certain materials or circumstances, it can become dominant effect limiting conductivity. In bulk materials, interface scattering is usually ignored.^{[8]}^{[9]}^{[10]}^{[11]}
Inelastic scattering
During inelastic scattering processes, significant energy exchange happens. As with elastic phonon scattering also in the inelastic case, the potential arouses from energy band deformations caused by atomic vibrations. Optical phonons causing inelastic scattering usually have the energy in the range 3050 meV, for comparison energies of acoustic phonon are typically less than 1 meV but some might have energy in order of 10 meV. There is significant change in carrier energy during the scattering process. Optical or highenergy acoustic phonons can also cause intervalley or interband scattering, which means that scattering is not limited within single valley. ^{[8]}
Electronelectron scattering
Due to the Pauli exclusion principle, electrons can be considered as noninteracting if their density does not exceed the value 10^{17} cm^{3} or electric field value 10^{3} V/cm. However, significantly above these limits electronelectron scattering starts to dominate. Long range and nonlinearity of the Coulomb potential governing interactions between electrons make these interactions difficult to deal with. ^{[9]}^{[8]}^{[10]}
Relation between mobility and scattering time
A simple model gives the approximate relation between scattering time (average time between scattering events) and mobility. It is assumed that after each scattering event, the carrier's motion is randomized, so it has zero average velocity. After that, it accelerates uniformly in the electric field, until it scatters again. The resulting average drift velocity is:^{[12]}
where q is the elementary charge, m* is the carrier effective mass, and τ is the average scattering time.
If the effective mass is anisotropic (directiondependent), m* is the effective mass in the direction of the electric field.
Matthiessen's rule
Normally, more than one source of scattering is present, for example both impurities and lattice phonons. It is normally a very good approximation to combine their influences using "Matthiessen's Rule" (developed from work by Augustus Matthiessen in 1864):
 .
where µ is the actual mobility, μ_{impurities} is the mobility that the material would have if there was impurity scattering but no other source of scattering, and μ_{lattice} is the mobility that the material would have if there was lattice phonon scattering but no other source of scattering. Other terms may be added for other scattering sources, for example
 .
Matthiessen's rule can also be stated in terms of the scattering time:
 .
where τ is the true average scattering time and τ_{impurities} is the scattering time if there was impurity scattering but no other source of scattering, etc.
Matthiessen's rule is an approximation and is not universally valid. This rule is not valid if the factors affecting the mobility depend on with each other, because individual scattering probabilities cannot be summed unless they are independent of each other. The average free time of flight of a carrier and therefore the relaxation time is inversely proportional to the scattering probability. ^{[8]}^{[9]}^{[11]}For example, lattice scattering alters the average electron velocity (in the electricfield direction), which in turn alters the tendency to scatter off impurities. There are more complicated formulas that attempt to take these effects into account.^{[13]}
Temperature dependence of mobility
Typical temperature dependence of mobility^{[1]}
(depends on the temperature range and sample)Si Ge GaAs Electrons ∝T ^{−2.4} ∝T ^{−1.7} ∝T ^{−1.0} Holes ∝T ^{−2.2} ∝T ^{−2.3} ∝T ^{−2.1} With increasing temperature, phonon concentration increases and causes increased scattering. Thus lattice scattering lowers the carrier mobility more and more at higher temperature. Theoretical calculations reveal that the mobility in nonpolar semiconductors, such as silicon and germanium, is dominated by acoustic phonon interaction. The resulting mobility is expected to be proportional to T ^{−3/2}, while the mobility due to optical phonon scattering only is expected to be proportional to T ^{−1/2}. Experimentally, values of the temperature dependence of the mobility in Si, Ge and GaAs are listed in table.^{[1]}
As , where Σ is the scattering cross section for electrons and holes at a scattering center and is a thermal average (Boltzmann statistics) over all electron or hole velocities in the lower conduction band or upper valence band, temperature dependence of the mobility can be determined. In here, the following definition for the scattering cross section is used: number of particles scattered into solid angle dΩ per unit time divided by number of particles per area per time (incident intensity), which comes from classical mechanics. As Boltzmann statistics are valid for semiconductors .
For scattering from acoustic phonons for temperatures (Θ=Debye temperature), the estimated cross section Σ_{ph} is determined from the square of the average vibrational amplitude of a phonon to be proportional to T. The scattering from charged defects (ionized donors or acceptors) leads to the cross section . This formula is the scattering cross section for “Rutherford scattering”, where a point charge (carrier) moves past another point charge (defect) experiencing Coulomb interaction.
The temperature dependencies of these two scattering mechanism in semiconductors can be determined by combining formulas for τ, Σ and , to be for scattering from acoustic phonons μ_{ph}∼T ^{− 3 / 2} and from charged defects μ_{def}∼T^{3 / 2}. ^{[9]}^{[11]}
The effect of ionized impurity scattering, however, decreases with increasing temperature because the average thermal speeds of the carriers are increase.^{[7]} Thus, the carriers spend less time near an ionized impurity as they pass and the scattering effect of the ions is thus reduced.
These two effects operate simultaneously on the carriers through Matthiessen's rule. At lower temperatures, ionized impurity scattering dominates, while at higher temperatures, phonon scattering dominates, and the actual mobility reaches a maximum at an intermediate temperature.
Measurement of semiconductor mobility
Hall mobility
Main article: Hall effectCarrier mobility is most commonly measured using the Hall effect. The result of the measurement is called the "Hall mobility" (meaning "mobility inferred from a Halleffect measurement").
Consider a semiconductor sample with a rectangular cross section as shown in the figures, a current is flowing in the xdirection and a magnetic field is applied in the zdirection. The resulting Lorentz force will accelerate the electrons (ntype materials) or holes (ptype materials) in the (−y) direction, according to the right hand rule and set up an electric field ξ_{y}. As a result there is a voltage across the sample, which can be measured with a highimpedance voltmeter. This voltage, V_{H}, is called the Hall voltage. V_{H} is negative for ntype material and positive for ptype material.
Mathematically, the Lorentz force acting on a charge Q is given by
For electrons:
For holes:
In steady state this force is balanced by the force set up by the Hall voltage, so that there is no net force on the carriers in the y direction. For electron,


 ξ_{y} = v_{x}B_{z}

For electrons, the field points in the y direction, and for holes, it points in the +y direction.
The electron current I is given by I = − qnv_{x}tW. Sub v_{x} into the expression for ξ_{y},
where R_{Hn} is the Hall coefficient for electron, and is defined as
Since
Similarly, for holes
From Hall coefficient, we can obtain the carrier mobility as follows:
Similarly,
Here the value of V_{Hp} (Hall voltage), t (sample thickness), I (current) and B (magnetic field) can be measured directly, and the conductivities σ_{n} or σ_{p} are either known or can be obtained from measuring the resistivity.
Fieldeffect mobility
See also: MOSFETNot to be confused with Wien effect.The mobility can also be measured using a fieldeffect transistor (FET). The result of the measurement is called the "fieldeffect mobility" (meaning "mobility inferred from a fieldeffect measurement").
The measurement can work in two ways: From saturationmode measurements, or linearregion measurements.^{[14]} (See MOSFET for a description of the different modes or regions of operation.)
Using saturation mode
In this technique,^{[14]} for each fixed gate voltage V_{GS}, the drainsource voltage V_{DS} is increased until the current I_{D} saturates. Next, the square root of this saturated current is plotted against the gate voltage, and the slope m_{sat} is measured. Then the mobility is:
where L and W are the length and width of the channel and C_{i} is the gate insulator capacitance per unit area. This equation comes from the approximate equation for a MOSFET in saturation mode:
where V_{th} is the threshold voltage. This approximation ignores the Early effect (channel length modulation), among other things. In practice, this technique may underestimate the true mobility.^{[15]}
Using the linear region
In this technique,^{[14]} the transistor is operated in the linear region (or "ohmic mode"), where V_{DS} is small and with slope m_{lin}. Then the mobility is:
 .
This equation comes from the approximate equation for a MOSFET in the linear region:
In practice, this technique may overestimate the true mobility, because if V_{DS} is not small enough and V_{G} is not large enough, the MOSFET may not stay in the linear region.^{[15]}
Doping concentration dependence in heavilydoped silicon
The charge carriers in semiconductors are electrons and holes. Their numbers are controlled by the concentrations of impurity elements, i.e. doping concentration. Thus doping concentration has great influence on carrier mobility.
While there is considerable scatter in the experimental data, for noncompensated material (no counter doping) for heavily doped substrates (i.e. 10^{18}cm ^{− 3} and up), the mobility in silicon is often characterized by the empirical relationship:^{[16]}
where N is the doping concentration (either N_{D} or N_{A}), and N_{ref} and α are fitting parameters. At room temperature, the above equation becomes:
Majority carriers:^{[17]}
Minority carriers:^{[18]}
These equations apply only to silicon, and only under low field.
See also
References
 ^ ^{a} ^{b} ^{c} ^{d} Chapter 2: Semiconductor Fundamentals. Online textbook by B. Van Zeghbroeck]
 ^ Electrical properties of silicon, Ioffe Institute Database
 ^ Harris, J. J.; Foxon, C. T.; Barnham, K. W. J.; Lacklison, D. E.; Hewett, J.; White, C. (1987). "Twodimensional electron gas structures with mobilities in excess of 3×106 cm2 V−1 s−1". Journal of Applied Physics 61: 1219. Bibcode 1987JAP....61.1219H. doi:10.1063/1.338174.
 ^ Dürkop, T.; Getty, S. A.; Cobas, Enrique; Fuhrer, M. S. (2004). "Extraordinary Mobility in Semiconducting Carbon Nanotubes". Nano Letters 4: 35. Bibcode 2004NanoL...4...35D. doi:10.1021/nl034841q.
 ^ Bolotin, K; Sikes, K; Jiang, Z; Klima, M; Fudenberg, G; Hone, J; Kim, P; Stormer, H (2008). "Ultrahigh electron mobility in suspended graphene". Solid State Communications 146: 351. arXiv:0802.2389. Bibcode 2008SSCom.146..351B. doi:10.1016/j.ssc.2008.02.024.
 ^ ^{a} ^{b} Vladimir Vasilʹevich Mitin; Vi︠a︡cheslav Aleksandrovich Kochelap; Michael A. Stroscio (1999). Quantum heterostructures: microelectronics and optoelectronics. Cambridge University Press. pp. 307–9. ISBN 9780521636353. http://books.google.com/books?id=Wzo4IdxS48oC&pg=PA308. Retrieved 2 March 2011.
 ^ ^{a} ^{b} Singh. Electronic Devices And Integrated Circuits. PHI Learning Pvt. Ltd.. pp. 77–. ISBN 9788120331921. http://books.google.com/books?id=2aqtlybkFE0C&pg=PA77. Retrieved 1 March 2011.
 ^ ^{a} ^{b} ^{c} ^{d} ^{e} ^{f} ^{g} ^{h} Ferry, David K. Semiconductor transport. London: Taylor & Francis, 2000. ISBN 0748408657 (hbk.), ISBN 0748408665 (pbk.)
 ^ ^{a} ^{b} ^{c} ^{d} Ibach, Harald. ; Luth, Hans. Solidstate physics : an introduction to principles of materials science / Harald Ibach, Hans Luth. New York: Springer, 2009. (Advanced texts in physics) ISBN 9783540938033
 ^ ^{a} ^{b} A. Bulusu, D.G. Walker. Review of electronic transport models for thermoelectric materials, Superlattices and Microstructures, Volume 44, Issue 1, July 2008, Pages 136, ISSN 07496036, DOI: 10.1016/j.spmi.2008.02.008.
 ^ ^{a} ^{b} ^{c} Bhattacharya, Pallab. Semiconductor optoelectronic devices / Pallab Bhattacharya. Upper Saddle River (NJ): PrenticeHall, 1997. ISBN 0134956567 (nid.)
 ^ Peter Y. Yu; Manuel Cardona (30 May 2010). Fundamentals of Semiconductors: Physics and Materials Properties. Springer. pp. 205–. ISBN 9783642007095. http://books.google.com/books?id=5aBuKYBT_hsC&pg=PA205+. Retrieved 1 March 2011.
 ^ Antonio Luque; Steven Hegedus (9 June 2003). Handbook of photovoltaic science and engineering. John Wiley and Sons. p. 79, eq. 3.58. ISBN 9780471491965. http://books.google.com/books?id=ubCMhl_JjQC. Retrieved 2 March 2011. weblink (subscription only)
 ^ ^{a} ^{b} ^{c} Constance RostBietsch (August 2005). Ambipolar and LightEmitting Organic FieldEffect Transistors. Cuvillier Verlag. pp. 17–. ISBN 9783865375353. http://books.google.com/books?id=Xxvt0CkVKaIC&pg=PA17. Retrieved 1 March 2011.. This reference mistakenly leaves out a factor of 1/V_{DS} in eqn (2.11). The correct version of that equation can be found, e.g., in Stassen, A. F.; De Boer, R. W. I.; Iosad, N. N.; Morpurgo, A. F. (2004). "Influence of the gate dielectric on the mobility of rubrene singlecrystal fieldeffect transistors". Applied Physics Letters 85: 3899. arXiv:condmat/0407293. Bibcode 2004ApPhL..85.3899S. doi:10.1063/1.1812368.
 ^ ^{a} ^{b} Constance RostBietsch (August 2005). Ambipolar and LightEmitting Organic FieldEffect Transistors. Cuvillier Verlag. pp. 19–. ISBN 9783865375353. http://books.google.com/books?id=Xxvt0CkVKaIC&pg=PA19. Retrieved 20 April 2011. "Extracting the fieldeffect mobility directly from the linear region of the output characteristic may yield larger values for the fieldeffect mobility than the actual one, since the drain current is linear only for very small VDS and large VG. In contrast, extracting the fieldeffect mobility from the saturated region might yield rather conservative values for the fieldeffect mobility, since the draincurrent dependence from the gatevoltage becomes subquadratic for large VG as well as for small VDS."
 ^ B. L. Anderson and R. L. Anderson, "Fundamentals of Semiconductor Devices, " Mc Graw Hill, 2005
 ^ Caughey, D.M.; Thomas, R.E. (1967). "Carrier mobilities in silicon empirically related to doping and field". Proceedings of the IEEE 55: 2192. doi:10.1109/PROC.1967.6123.
 ^ Del Alamo, J (1985). "Measuring and modeling minority carrier transport in heavily doped silicon". SolidState Electronics 28: 47. Bibcode 1985SSEle..28...47D. doi:10.1016/00381101(85)902096.
External links
 The minority Carrier Lifetime in silicon wafer
 semiconductor glossary entry for electron mobility
 Resistivity and Mobility Calculator from the BYU Cleanroom
 Online lecture Mobility from an atomistic point of view
Categories: Physical quantities
 Condensed matter physics
 Materials science
 Semiconductors
 Electric and magnetic fields in matter
Wikimedia Foundation. 2010.
Look at other dictionaries:
electron mobility — elektronų judris statusas T sritis chemija apibrėžtis Dydis, lygus elektronų judėjimo greičiui, įgyjamam 1 V/m stiprio elektriniame lauke. atitikmenys: angl. electron mobility; electronic mobility rus. подвижность электронов … Chemijos terminų aiškinamasis žodynas
electron mobility — elektronų judris statusas T sritis Standartizacija ir metrologija apibrėžtis Dydis, lygus elektronų judėjimo greičiui, įgyjamam 1 V/m stiprio elektriniame lauke. atitikmenys: angl. electron mobility vok. Elektronenbeweglichkeit, f rus.… … Penkiakalbis aiškinamasis metrologijos terminų žodynas
electron mobility — elektronų judris statusas T sritis fizika atitikmenys: angl. electron mobility vok. Elektronenbeweglichkeit, f rus. подвижность электронов, f pranc. mobilité d’électrons, f; mobilité électronique, f … Fizikos terminų žodynas
High Electron Mobility Transistor — HEMT stands for High Electron Mobility Transistor, and is also called heterostructure FET (HFET) or modulation doped FET (MODFET). A HEMT is a field effect transistor incorporating a junction between two materials with different band gaps (i.e. a … Wikipedia
Induced high electron mobility transistor — In contrast to a modulation doped HEMT, an induced high electron mobility transistor provides the flexibility to tune different electron densities with a top gate. Since the charge carriers are induced to the 2DEG plane rather than created by… … Wikipedia
Highelectronmobility transistor — Querschnitt eines InGaAs pseudomorphen HEMT Der high electron mobility transistor (HEMT, dt. »Transistor mit hoher Elektronenbeweglichkeit«) ist eine spezielle Bauform des Feldeffekttransistors für sehr hohe Frequenzen und ist von der… … Deutsch Wikipedia
High Electron Mobility Transistor — Der High Electron Mobility Transistor (HEMT, dt. »Transistor mit hoher Elektronenbeweglichkeit«) ist eine spezielle Bauform des Feldeffekttransistors für sehr hohe Frequenzen und ist von der Konstruktion her eine spezielle Bauform eines JFETs.… … Deutsch Wikipedia
highelectron mobility transistor — didelio elektronų judrio tranzistorius statusas T sritis radioelektronika atitikmenys: angl. high electron mobility transistor vok. Transistor mit hoher Elektronenbeweglichkeit, m rus. транзистор с высокой подвижностью электронов, m pranc.… … Radioelektronikos terminų žodynas
Mobility — may refer to: Mobility (computer game) Mobiliy (song), a song by Moby Mobility (chess) Mobility (military), the ability of military units or weapon systems to move to an objective See also Academic mobility Apprentices mobility Economic mobility… … Wikipedia
Electron bubble — An electron bubble is the empty space created around a free electron in a cryogenic gas or liquid, such as neon or helium. They are typically very small, about 2 nm in diameter at atmospheric pressure.Electron bubbles in heliumAt room temperature … Wikipedia