Ceramic forming techniques

Ceramic forming techniques are ways of forming ceramic shapes. This can be used to make everyday tableware from teapots, to engineering ceramics such as computer parts. Methods for forming powders of ceramic raw materials into complex shapes are desirable in many areas of technology. For example, such methods are required for producing advanced, high-temperature structural parts such as heat engine components, recuperators and the like from powders of ceramic raw materials. Typical parts produced with this production operation include impellers made from stainless steel, bronze, complex cutting tools, plastic mould tooling, and others. Typical materials used are: wood, metal, water, plaster, epoxy and STLs, silica, and zirconia. This production operation is well known for providing tools with dimensional stability, surface quality, density and uniformity. For instance, on the slip casting process the cast part is of high concentration of raw materials with little additive, this improves uniformity. But also, the plaster mould draws water from the poured slip to compact and form the casting at the mould surface. This forms a dense cast.

Contents

Forming Techniques

There are many forming techniques to make ceramics, but one example is slipcasting. This is where slip, liquid clay, is poured into a plaster mould. The water in the slip is drawn out of the slip, leaving an inside layer of solid clay. When this is thick enough, the excess slip can be removed from the mould. When dry, the solid clay can then also be removed. The slip used in slip casting is often liquified with a substance that reduces the need for additional water to soften the slip; this prevents excessive shrinkage which occurs when a piece containing a lot of water dries.

Slip Casting

Slip-casting methods provide superior surface quality, density and uniformity in casting high-purity ceramic raw materials over other ceramic casting techniques, such as hydraulic casting, since the cast part is a higher concentration of ceramic raw materials with little additives. A slip is a suspension of fine raw materials powder in a liquid such as water or alcohol with small amounts of secondary materials such as dispersants, surfactants and binders. Early slip casting techniques employed a plaster block or flask mould. The plaster mould draws water from the poured slip to compact and form the casting at the mould surface. This forms a dense cast form removing deleterious air gaps and minimizing shrinkage in the final sintering process.

Ceramic Shell Casting

Ceramic shell casting techniques using silica, zirconia and other refractory materials are currently used by the metal parts industry for `net casting`, forming precision shell moulds for molten metal casting. The technique involves a successive wet dipping and dry powder coating or stucco to build up the mould shell layer. The shell casting method in general is known for dimensional stability and is used in many net-casting processes for aerospace and other industries in molten metal casting. Automated facilities use multiple wax patterns on trees, large slurry mixers and fluidic powder beds for automated dipping.

Other Techniques

There are also several traditional techniques of handbuilding, such as pinching, soft slab, hard slab, and coil construction.

Other techniques involve threading animal or artificial wool fibre through paperclay slip, to build up layers of material. The result can be wrapped over forms or cut, dried and later joined with liquid and soft paperclay.

When forming very thin sheets of ceramic material, "tape casting" is commonly used. This involves pouring the slip (which contains a polymer "binder" to give it strength) onto a moving carrier belt, and then passing it under a stationary "doctor blade" to adjust the thickness. The moving slip is then air dried, and the "tape" thus formed is peeled off the carrier belt, cut into rectangular shapes, and processed further. As many as 100 tape layers, alternating with conductive metal powder layers, can be stacked up. These are then sintered ("fired") to remove the polymer and thus make "multilayer" capacitors, sensors, etc. According to D. W. Richerson of the American Ceramic Society, more than a billion of such capacitors are manufactured every day. (About 100 are in a typical cellular telephone, and about a thousand in a typical automobile.)

Technical Ceramics

When forming technical ceramic materials from dry powders prepared for processing, the method of forming into the shape required depends upon the method of material preparation and size and shape of the part to be formed. Materials prepared for dry powder forming are most commonly formed by "dry" pressing in mechanical or hydraulic powder compacting presses selected for the necessary force and powder fill depth. Dry powder is automatically discharged into the non-flexible steel or tungsten carbide insert in the die and punches then compact the powder to the shape of the die. If the part is to be large and unable to have pressure transmit suitably for a uniform pressed density then isostatic pressing may be used. When iso-statically pressed the powder takes the shape of a flexible membrane acting as the mould, forming the shape and size of the pressed powder. Isostatic presses can be either high speed, high output type of automatic presses for such parts as ceramic insulators for spark plugs or sand blast nozzles, or slower operating "wet bag" presses that are much more manual in operation but suitable particularly for large machinable blanks or blanks that will be cut or otherwise formed in secondary operations to the final shape.

If technical ceramic parts are needed where the length to diameter ratio is very large, extrusion may be used. There are two types of ceramic extruders one being piston type with hydraulic force pushing a ram that in turn is pushing the ceramic through the loaded material cylinder to and through the die which forms the extrudate. The second type of extruder is a screw, or auger, type where a screw turns forcing the material to and through the die which again shapes the part. In both types of extrusion the raw material must be plasticized to allow and induce the flow of the material in the process.

Complex technical ceramic parts are commonly formed using either the injection moulding process or a process known as "hot wax moulding" both of which rely upon heat sensitive plasticizers to allow flow of the material into a die which forms the part. The part is then quickly cooled for removal from the die. The injection moulding process is much like injection moulding of plastic materials using various polymers for plasticizing while the hot wax moulding process largely uses paraffin wax.

There are also many more techniques, such as gel casting and injection moulding that are often used to create engineering ceramics.

External links


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • Ceramic materials — Ceramic Si3N4 bearing parts Ceramic materials are inorganic, non metallic materials and things made from them. They may be crystalline or partly crystalline. They are formed by the action of heat and subsequent cooling.[1] Clay was one of the… …   Wikipedia

  • Ceramic engineering — Simulation of the outside of the Space Shuttle as it heats up to over 1,500 °C (2,730 °F) during re entry into the Earth s atmosphere Ceramic engineering is the science and technology of creating objects from inorganic, non metallic… …   Wikipedia

  • Ceramic — A Ming Dynasty porcelain vase dating 1403 1424 …   Wikipedia

  • Ceramic molding — The ceramic molding process is an easy production method which guarantees the precision required, and also gives a good surface finish, using a high temperature method to better structure and shape parts. This process also gives a low grade of… …   Wikipedia

  • Ceramic matrix composite — Fracture surface of a fiber reinforced ceramic composed of SiC fibers and SiC matrix. The fiber pull out mechanism shown is the key to CMC properties …   Wikipedia

  • Ceramic mold casting — Ceramic mold casting, also known ambiguously as ceramic molding,[1] is a group of metal casting processes that use ceramics as the mold material. It is a combination of plaster mold casting and investment casting.[2][3] There are two types of… …   Wikipedia

  • Ceramic glaze — Composite body, painted, and glazed bottle. Dated 16th century. From Iran. New York Metropolitan Museum of Art. Glaze is a layer or coating of a vitreous substance which has been fired to fuse to a ceramic object to color, decorate, strengthen or …   Wikipedia

  • Spray forming — Spray forming, also known as spray casting, spray deposition[1] and in situ compaction,[2] is a method of casting near net shape metal components with homogeneous microstructures via the deposition of semi solid sprayed droplets onto a shaped… …   Wikipedia

  • Egyptian pyramid construction techniques — There have been many hypotheses about the Egyptian pyramid construction techniques. The construction techniques seem to have developed over time; the earliest pyramids were built in different ways than later ones. Most of the construction… …   Wikipedia

  • Porcelain — Fine China redirects here. For the band, see Fine China (band). This article is about the ceramic material. For other uses, see Porcelain (disambiguation). Chinese moon flask, 1723 35, Qing Dynasty …   Wikipedia


We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.