Sulfide stress cracking

Sulfide stress cracking

Sulfide stress cracking, or sulfide stress corrosion cracking (SSCC), is a special corrosion type, a form of stress corrosion cracking. Susceptible alloys, especially steels, react with hydrogen sulfide, forming metal sulfides and elementary atomic hydrogen. Atomic hydrogen, created as a product of a cathodic reaction in the presence of H2S, diffuses into the metal matrix.

High content of nickel in the steels greatly improves their resistance to SSC. This type of corrosion is worst at temperatures around 80 °C (176 °F).

Sulfide stress cracking has special importance in gas and oil industry, as the materials being processed there (natural gas and crude oil) often contain considerable amount of hydrogen sulfide. Equipment that comes in contact with such high-sulfur materials has to be rated for sour service NACE TM0177-96 Standard .

"High Temperature Hydrogen Attack" does not rely on atomic hydrogen. At high temperature and high hydrogen partial pressure, hydrogen can diffuse into carbon steel alloys. In susceptible alloys, the hydrogen combines with carbon within the alloy and forms methane. The methane molecules create a pressure which leads to embrittlement and even cracking of the metal.

SSC is a low temperature (temperature where water is liquid) effect of H2S in an aqueous environment and Sulfidation is the term used for the high temperature (>450F) sulfur corrosion.


Wikimedia Foundation. 2010.

Игры ⚽ Поможем решить контрольную работу

Look at other dictionaries:

  • Sulfide stress cracking — Sulfide stress cracking. См. Трещинооб разование от коррозии с сульфидами под напряжением. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • Sulfide — For other uses, see Sulphide (disambiguation). Sulfide Systematic name Sulfanediide …   Wikipedia

  • Трещинооб-разование от коррозии с сульфидами под напряжением — Sulfide stress cracking (SCC) Трещинооб разование от коррозии с сульфидами под напряжением. Хрупкий излом вследствие возникновения трещины при совместном воздействии растягивающего напряжения и коррозии в присутствии воды и сульфида водорода.… …   Словарь металлургических терминов

  • Corrosion — v · d · e Materials failure modes Buckling · …   Wikipedia

  • Metallurgical failure analysis — is the process by which a metallurgist determines the mechanism that has caused a metal component to fail. Typical failure modes involve various types of corrosion and mechanical damage. It has been estimated that the direct annual cost of… …   Wikipedia

  • Hydrogen embrittlement — (or hydrogen grooving) is the process by which various metals, most importantly high strength steel, become brittle and crack following exposure to hydrogen. Hydrogen cracking can pose an engineering problem especially in the context of a… …   Wikipedia

  • Embrittlement — is a loss of ductility of a material, making it brittle. Various materials have different mechanisms of embrittlement.* Hydrogen embrittlement is the effect of hydrogen absorption on some metals and alloys.* Sulfide stress cracking is the… …   Wikipedia

  • ГОСТ Р 53679-2009: Нефтяная и газовая промышленность. Материалы для применения в средах, содержащих сероводород, при добыче нефти и газа. Часть 1. Общие принципы выбора материалов, стойких к растрескиванию — Терминология ГОСТ Р 53679 2009: Нефтяная и газовая промышленность. Материалы для применения в средах, содержащих сероводород, при добыче нефти и газа. Часть 1. Общие принципы выбора материалов, стойких к растрескиванию оригинал документа: 3.1… …   Словарь-справочник терминов нормативно-технической документации

  • Sour gas — is natural gas or any other gas containing significant amounts of hydrogen sulfide (H2S). Natural gas is usually considered sour if there are more than 5.7 milligrams of H2S per cubic meter of natural gas, which is equivalent to approximately 4… …   Wikipedia

  • Acid gas — is natural gas or any other gas mixture which contains significant amounts of hydrogen sulfide (H2S), carbon dioxide (CO2), or similar contaminants. The terms acid gas and sour gas are often incorrectly treated as synonyms. Strictly speaking, a… …   Wikipedia