Riser (casting)

Riser (casting)
A bronze casting showing the sprue and risers

A riser, also known as a feeder,[1] is a reservoir built into a metal casting mold to prevent cavities due to shrinkage. Most metals are less dense as a liquid than as a solid so castings shrink upon cooling, which can leave a void at the last point to solidify. Risers prevent this by providing molten metal to the casting as it solidifies, so that the cavity forms in the riser and not the casting.[2] Risers are not effective on materials that have a large freezing range, because directional solidification is not possible. They are also not needed for casting processes that utilized pressure to fill the mold cavity.[3] A feeder operated by a treadle is called an underfeeder.[4]

The activity of planning of how a casting will be gated and risered is called foundry methoding or foundry engineering.[citation needed]

Contents

Theory

Risers are only effective if three conditions are met: the riser cools after the casting, the riser has enough material compensate for the casting shrinkage, and the casting directionally solidifies towards the riser.

For the riser to cool after the casting the riser must cool more slowly than the casting. Chvorinov's rule briefly states that the slowest cooling time is achieved with the greatest volume and the least surface area; geometrically speaking, this is a sphere. So, ideally, a riser should be a sphere, but this isn't a very practical shape to insert into a mold, so a cylinder is used instead. The height to diameter ratio of the cylinder varies depending on the material, location of the riser, size of the flask, etc.[5]

The shrinkage must be calculated for the casting to confirm that there is enough material in the riser to compensate for the shrinkage. If it appears there is not enough material then the size of the riser must be increased. This requirement is more important for plate-like shapes, while the first requirement is more important for chunky shapes.[citation needed]

Finally, the casting must be designed to produce directional solidification, which sweeps from the extremities of the mold cavity toward the riser(s). In this way, the riser can feed molten metal continuously to part of the casting that is solidifying.[2] One part of achieving this end is by placing the riser near the thickest and largest part of the casting, as that part of the casting will cool and solidify last.[5] If this type of solidification is not possible, multiple risers that feed various sections of the casting or chills may be necessary.[3]

Types

Different types of risers

Risers are categorized based on three criteria: location, if it is open to the atmosphere, and how it is filled. If the riser is located on the casting then it is known as a top riser, but if it is located next to the casting it is known as a side riser. Top risers are advantageous because they take up less space in the flask than a side riser, plus they have a shorter feeding distance. If the riser is open to the atmosphere it is known as an open riser, but if the risers is completely contained in the mold it is known as a blind riser. A blind riser is usually bigger than an open riser because the blind riser loses more heat to mold through the top of the riser. Finally, if the riser receives material from the gating system and fills after the mold cavity it is known as a live riser or hot riser. If the riser fills with material that has already flowed through the mold cavity it is known as a dead riser or cold riser. Live risers are usually smaller than dead risers. Note that top risers are almost always dead risers and risers in the gating system are almost always live risers.[5]

Note that the connection of the riser to the molding cavity can be an issue for side risers. On one hand the connection should be as small as possible to make separation as easy as possible, but, on the other, the connection must be big enough for it to not solidify before the riser. The connection is usually made short to take advantage of the heat of both the riser and the molding cavity, which will keep it hot throughout the process.[3]

There are risering aids that can be implemented to slow the cooling of a riser or decrease its size. One is using an insulating sleeve and top around the riser. Another is placing a heater around only the riser.[3]

Hot tops

A hot top, also known as a feeder head,[6] is a specialized riser that is used when casting ingots. It is essentially a live open riser, except a hot ceramic liner is used instead of just the mold material. The ingot is mostly poured and then the hot top is placed at the top of the mold. The rest of the metal is then poured.[7] This keeps piping to a minimum. Robert Forester Mushet invented the hot top, but then called it a dozzle. With a hot top only 1 to 2% of the ingot is waste, prior up to 25% of the ingot was wasted.[8]

Yield

The efficiency, or yield, of a casting is defined as the weight of the casting divided by the weight of the total amount of metal poured. Risers can add a lot to the total weight being poured, so it is important to optimize their size and shape. Because risers exist only to ensure the integrity of the casting, they are removed after the part has cooled, and their metal is remelted to be used again. As a result, riser size, number, and placement should be carefully planned to reduce waste while filling all the shrinkage in the casting.[5]

One way to calculate the minimum size of a riser is to use Chvorinov's rule by setting the solidification time for the riser to be longer than that of the casting. Any time can be chosen but 25% longer is usually a safe choice, which is written as follows:[5]

triser = 1.25tcasting

or

\left( \frac{V}{A} \right)^n_\text{riser} = 1.25\left( \frac{V}{A} \right)^n_\text{casting}

Because all of the mold and material factors are the same for n. If a cylinder is chosen for the geometry of the riser and the height to diameter ratio is locked, then the equation can be solved for a diameter, which makes this method a simple way to calculate the minimum size for a riser. Note that if a top riser is used the surface area that is shared between the riser and the casting should be subtracted from the area on the casting and the riser.[9]

References

  1. ^ Ravi 2005, p. 63.
  2. ^ a b Degarmo 2003, p. 286.
  3. ^ a b c d Degarmo 2003, p. 288.
  4. ^ George Hogarth Makins (1862), A Manual of Metallurgy: More Particularly of the Precious Metals, but Including Such Others as are Employed in Dental Practice, F.S. Ellis, p. 77, http://books.google.com/?id=QR1IAAAAIAAJ&pg=PP1#v=onepage&q= 
  5. ^ a b c d e Degarmo 2003, p. 287.
  6. ^ Cmj Network, Inc (06-25-1959), "Riser filled by electro-slag welding", The New Scientist 5 (136): 1383, http://books.google.com/books?id=tkhxef8vbzMC&lpg=PA1383 
  7. ^ Oberg, Erik; Jones, Franklin Day (1920), Iron and steel, Industrial Press, p. 129, http://books.google.com/books?id=dO8DAQAAIAAJ&pg=PA129. 
  8. ^ Gordon, Robert (1996), American Iron, 1607-1900, Johns Hopkins University Press, p. 178, ISBN 9780801868160, http://books.google.com/books?id=osSG7ceTGekC&lpg=PA178 
  9. ^ Degarmo 2003, pp. 287–288.

Bibliography


Wikimedia Foundation. 2010.

Игры ⚽ Нужен реферат?

Look at other dictionaries:

  • Casting (metalworking) — Casting iron in a sand mold In metalworking, casting involves pouring liquid metal into a mold, which contains a hollow cavity of the desired shape, and then allowing it to cool and solidify. The solidified part is also known as a casting, which… …   Wikipedia

  • Riser — may refer to: Riser (casting), a reservoir in a manufacturing mold Stair riser, the vertical elements in a set of stairs Drilling riser, a device used on a ship or offshore drilling rig Neil Riser, a member of the Louisiana State Senate (United… …   Wikipedia

  • Casting defect — A casting defect is an irregularity in the metal casting process that is undesired. Some defects can be tolerated while others can be repaired otherwise they must be eliminated. They are broken down into five main categories: gas porosity,… …   Wikipedia

  • riser — Shrinking Shrink ing, a. & n. from {Shrink}. [1913 Webster] {Shrinking head} (Founding), a body of molten metal connected with a mold for the purpose of supplying metal to compensate for the shrinkage of the casting; called also {sinking head},… …   The Collaborative International Dictionary of English

  • riser — Feed Feed, n. 1. That which is eaten; esp., food for beasts; fodder; pasture; hay; grain, ground or whole; as, the best feed for sheep. [1913 Webster] 2. A grazing or pasture ground. Shak. [1913 Webster] 3. An allowance of provender given to a… …   The Collaborative International Dictionary of English

  • Chill (casting) — A chill is an object used to promote solidification in a specific portion of a metal casting mold. Normally the metal in the mold cools at a certain rate relative to thickness of the casting. When the geometry of the molding cavity prevents… …   Wikipedia

  • Die casting — An engine block with aluminium and magnesium die castings. Die casting is a metal casting process that is characterized by forcing molten metal under high pressure into a mold cavity. The mold cavity is created using two hardened tool steel dies… …   Wikipedia

  • Sand casting — Sand casting, also known as sand molded casting, is a metal casting process characterized by using sand as the mold material. It is relatively cheap and sufficiently refractory even for steel foundry use. A suitable bonding agent (usually clay)… …   Wikipedia

  • Continuous casting — The macrostructure of continuously cast copper (99.95% pure), etched, ∅ ≈ 83 mm. Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a semifinished billet, bloom, or slab for subsequent rolling… …   Wikipedia

  • Lost-foam casting — (LFC) is a type of investment casting process that uses foam patterns as the investment. This method takes advantage of the properties of foam to simply and cheaply form castings that would be difficult or impossible, using normal cope and drag… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”