- High temperature insulation wool
-
Microscopic close-up of ceramic fibre.
HTIW modules.
Industrial furnace equipped with HTIW modules.
Industrial furnace equipped with HTIW in operation.
Temperature ranges for the application of HTIW
Applications of Alkaline Earth Silicate Wool sorted by sector (in the EU)
Applications of Alumino Silicate Wool sorted by sector (in the EU)
Applications of Polycristalline Wool sorted by sector (in the EU)
Comparison of traditional and modern refractoriesIn the 1950s, the term “Refractory Ceramic Fibre” was coined for the aluminium silicate fibres developed at this time. On account of their chemical purity and resistance to high temperatures (classification temperature >1000 °C) as well as on the basis of their use in other applications, this definition was made to differentiate aluminium silicate wools from the conventional “mineral wools”. Because of the ambiguity of the term “ceramic” and the development of new materials for the high temperature range, the nomenclature was changed to High Temperature Insulation Wool (HTIW) at the end of the 1990s.
Basically, there are two types of inorganic HTIW. In addition to the more commonly used amorphous HTIW (Alumino Silicate Wool ASW/RCF and Alkaline Earth Silicate Wool (AES)), Polycrystalline Wool (PCW) is also available. Owing to the costly production and limited availability compared to mineral wool, HTIW products are almost only used in industrial applications and processes up to 1800 °C.
Contents
History
Man has used fire for melting and heat treating metals for thousands of years. To ensure safe working with the fire, for melting and working metals (bronze, iron), special refractory materials were needed to enable the handling of liquid or hot metals . To meet the needs of the wide-ranging applications, a large number of shaped, dense materials (refractory bricks, chamotte), shaped heat-insulating materials (lightweight refractory bricks) and unshaped refractory materials (heavy- and lightweight ramming mixes) have been developed, which are used for special high temperature applications. For decades, however, other manmade materials have been used for thermal insulation, glass wool and rock wool being used in the low-temperature range (around 200°C to maximum 500°C).
In the 1960s aluminium-silicate-based "Refractory Ceramic Fibre" were launched on the market in Europe. Due to their high temperature-resistance and good technical properties (i.e. good thermal shock resistance and low thermal conductivity), they quickly became the reference for industrial high temperature insulation. Due to the development of new material types the nomenclature of High Temperature Insulation Wool was redefined in Germany at the end of the 1990s. (VDI 3469.[1]). Although even today the term "Ceramic Fibre" or "Refractory Ceramic Fibre" is commonly used it is inaccurate in terms of the materials available, their specific properties and limitations.
Thermal insulation with HTIW enabled a more lightweight construction of industrial furnaces and other technical equipment (heating systems, automobiles), resulting in many economic and ecological benefits. Consequences are smaller wall thicknesses and considerably lower lining masses.
Comparison of the mass for the different wall linings
- Heavyweight lining: 1500 to 3500 kg/m³,
- Lightweight lining: 500 to 1000 kg/m³,
- Lining with HTIW: 160 to 300 kg/m³.
High Temperature Insulation Wool (HTIW)
High Temperature Insulation Wool is an accumulation of fibres of different lengths and diameters, produced synthetically from mineral raw materials. The group of the HTIWs include amorphous Alkaline Earth Silicate Wool (AES) and Aluminom Silicate Wool (ASW) as well as Polycrystalline Wool (PCW) (VDI 3469;[1] DIN-EN 1094) with a classification temperatures >1000 °C. Besides the differences in the chemical composition, manmade fibres have parallel edges in contrast to natural fibres.
Alkaline Earth Silicate Wool (AES Wool)
Also known as “High Temperature Glass Wool" (HTGW), AES Wool consist of amorphous fibres, which are produced by melting a combination of CaO-, MgO-, SiO2 and ZrO2 (see also VDI 3469, Parts 1 and 5[1]). Products made from AES are generally used at application temperatures less than 900 °C and in continuously operating equipment and domestic appliances.
Alumino Silicate Wool (ASW)
Alumino Silicate Wool, also known as “Refractory Ceramic Fibre” (RCF), are amorphous fibres produced by melting a combination of Al2O3 and SiO2, usually in a weight ratio 50:50 (see also VDI 3469 Parts 1 and 5,[1] as well as TRGS 521). Products made of Aluminom Silicate Wool are generally used at application temperatures >900°C and in intermittently operating equipment and critical application conditions (see Technical Rules TRGS 619).
Polycrystalline Wool (PCW)
Polycrystalline Wool consists of fibres containing greater than 70 wt.% Al2O3; they are produced by a "sol-gel method" from aqueous spinning solutions. The water-soluble green fibres obtained as a precursor are crystallized by means of heat treatment (see also VDI 3469 Parts 1 and 5[1]). Polycrystalline Wool is generally used at application temperatures greater than 1300 °C and in critical chemical and physical application conditions, also at lower temperatures.
HTIW and REACH
Registration, Evaluation, Authorisation and Restriction of Chemicals (REACH) is a European Union Regulation of 18 December 2006. REACH addresses the production and use of chemical substances, and their potential impacts on both human health and the environment. A Substance Information Exchange Forum (SIEF) has been set up for each type of HITW. AES, ASW and PCW have been registered before the first deadline of 1 December 2010 and can therefore be used on the European market.
Definitions
Classification Temperature
The classification temperature is defined as the temperature at which a linear shrinkage of 4% is not exceeded after 24 hour heat treatment in the electrically heated laboratory oven and in a neutral atmosphere. Depending on the type of product, the value may not exceed the following limits: 2% for boards and shaped products, 4% for mats and papers. The classification temperature is specified in 50°C steps (starting at 850 °C and up to 1600 °C). The classification temperature does not mean that the product can be used continuously at this temperature. In the field, the continuous application temperature of amorphous HTIW (AES and ASW) is typically 100 °C to 150 °C below the classification temperature. Products made of Polycrystalline Wool can generally be used up to classification temperature.
Wool
Wool is the term used to describe an ordered accumulation of fibres of varying length and diameter. HTIW fulfil this definition and are therefore covered by the term “wool”. Amorphous AES and ASW are produced by melting the raw materials in a melting pot by means of electrical resistance melting. The jet of melt discharged from the pot is accelerated in a blowing or spinning process and pulled into fibres with different length/diameter ratios.
Continuous fibres/textile glass fibres (VDI 3469 Part 1)
These fibres are produced by means of the continuous filament process with defined nozzle diameters, all fibres having the technical defined and required diameter. During handling, only fibres of the given diameter but different length are released.
Health hazards
Fibrous Dust
Driven by the health effects of Asbestos, extensive research has been conducted to evaluate the potential toxicity of many fibrous materials.
Some dusts if inhaled over a longer period may cause lung disease. Fibrous dust can be released during handling and working with Manmade Mineral and High Temperature Insulation Wool. Fibres with a length exceeding 5 µm, a diameter below 3 µm and a length to diameter ratio that is larger than 3:1 are regarded as respirable. Consequently, regulations on handling and use must be observed that are drawn up and published by the Federal Ministry of Labour and Social Affairs|Federal Ministry of Labour and the associations of the producers of high-temperature insulation wool. Detailed specifications are currently in preparation and will be added.
Research carried out in the European ASW manufacturing industry by the Institute of Occupational Medicine has shown that there was no indication of serious changes in chest x-rays of workers.[2] However, lung forced expired volume in 1 second (FEV1) and forced vital capacity (FVC) decreased with increasing exposure to airborne respirable fibres. Chronic bronchitis and its associated symptoms (cough, phlegm) showed some association with recent exposure to respirable fibres. Changes to the lung pleura seen on the chest radiographs, including pleural plaques, were related to age and exposure to asbestos. Amongst those men who had not worked with asbestos the prevalence of changes increased with increasing time since first exposure to airborne ASW fibres.
Crystalline Silica
Amorphous HTIW (AES and ASW) are produced from a molten glass stream which is aerosolised by a jet of high pressure air or by letting the stream impinge onto spinning wheels. The droplets are drawn into fibres; the mass of both fibres and remaining droplets cool very rapidly so that no crystalline phases form.
When amorphous HTIW are installed and used in high temperature applications such as industrial furnaces, at least one face may be exposed to conditions causing the fibres to partially devitrify. Depending on the chemical composition of the glassy fibre and the time and temperature to which the materials are exposed, different stable crystalline phases may form.
In after-use HTIW crystalline silica crystals are embedded in a matrix composed of other crystals and glasses. Experimental results on the biological activity of after-use HTIW have not demonstrated any hazardous activity that could be related to any form of silica they may contain.
References
- ^ a b c d e VDI Guideline: VDI 3469 Part 1 - Overview Part 5 – High-Temperature Insulation Wool
- ^ Cowie et al. An epidemiological study of the respiratory health of workers in the European refractory ceramic fibre industry. Occup Environ Med (2001) vol. 58 (12) pp. 800-10.
External links
Categories:- Refractory materials
Wikimedia Foundation. 2010.