Alkali Silica Reaction

Alkali Silica Reaction

Alkali-Silica Reaction (ASR) is a reaction between reactive silica (in the concrete aggregates) and an alkali (usually present in the cement), which results in the formation of a gel. This gel increases in volume with water and exerts expansive pressure on the concrete, causing failure of the concrete.

ASR can cause serious expansion and cracking in concrete, resulting in critical structural problems that can even force the demolition of a particular structure. [cite web | publisher = Understanding Cement | url = http://www.understanding-cement.com/alkali-silica.html | title = Alkali-silica reaction in concrete | accessdate = 2007-08-11]

The following is the mechanism of ASR causing the deterioration of concrete. 1) The alkaline solution attacks the surface of the siliceous aggregate to convert it to viscous alkali silicate gel. The aggregate is covered with the gel. 2) Consumption of alkali by the reaction induces the dissolution of Ca ions into the solution, which then react with the gel to convert it to hard calcium silicate (reaction rim). 3) The reaction rim allows the penetration of not the alkali silicate but the alkaline solution. The penetrated alkaline solution converts the remaining siliceous minerals into bulky alkali silicate gel. The resultant expansive pressure is stored in the aggregate. 4) The accumulated pressure cracks the aggregate and the surrounding cement paste when the pressure exceeds the tolerance of the aggregate [Modified model of Alkali-silica reaction T. Ichikawa, M. Miura, Cement and Concrete Research, 37 (2007) 1291–1297] .

ASR is eliminated in concrete by three approaches:
* Limit the alkali metal content of the cement. Many standards impose limits on the "Equivalent Na2O" content of cement.
* Limit the reactive silica content of the aggregate. Certain volcanic rocks are particularly susceptible to ASR because they contains volcanic glass (obsidian). In principle, pure limestone (CaCO3) are not expected to contain high level of silica. However, some limestones (e.g., Kieselkalk) may be cemented by amorphous silica and can be very sensitive to the ASR reaction such as observed with the limestone of the area of Tournai in Belgium.
* Add fine siliceous materials such as fly ashs to the mix. These react preferentially with the cement alkalis without formation of an expansive pressure, because siliceous minerals in fine particles totally convert to alkali silicate without formation of semipermeable reaction rims.

References


Wikimedia Foundation. 2010.

Игры ⚽ Поможем сделать НИР

Look at other dictionaries:

  • Alkali metal — Group → 1 ↓ Period 2 3 Li 3 …   Wikipedia

  • acid–base reaction — ▪ chemistry Introduction       a type of chemical process typified by the exchange of one or more hydrogen ions, H+, between species that may be neutral (molecules, such as water, H2O; or acetic acid, CH3CO2H) or electrically charged (ions, such… …   Universalium

  • Reinforced concrete — is concrete in which reinforcement bars ( rebars ), reinforcement grids, plates or fibers have been incorporated to strengthen the concrete in tension. It was invented by French gardener Joseph Monier in 1849 and patented in 1867.[1] The term… …   Wikipedia

  • Fly ash — Photomicrograph made with a Scanning Electron Microscope (SEM): Fly ash particles at 2,000x magnification Fly ash is one of the residues generated in combustion, and comprises the fine particles that rise with the flue gases. Ash which does not… …   Wikipedia

  • Metakaolin — is a dehydroxylated form of the clay mineral kaolinite. Rocks that are rich in kaolinite are known as china clay or kaolin, traditionally used in the manufacture of porcelain. The particle size of metakaolin is smaller than cement particles, but… …   Wikipedia

  • Protection of exposed concrete — is necessary to prolong its service life. A 120 year design life for concrete infrastructure has become increasingly common. Without early preventive maintenance this design life target may be optimistic. The design service life of reinforced… …   Wikipedia

  • Concrete degradation — may have various causes. Concrete can be damaged by fire, aggregate expansion, sea water effects, bacterial corrosion, calcium leaching, physical damage and chemical damage (from carbonation, chlorides, sulfates and distilled water). This process …   Wikipedia

  • Concrete step barrier — A concrete step barrier is a safety barrier used on the central reservation of motorways and dual carriageways as an alternative to the standard steel crash barrier. Concrete step barrier cross section The barrier has contained all vehicles up to …   Wikipedia

  • A38 road — A38 road …   Wikipedia

  • Construction aggregate — Limestone quarry …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”