Magnetocrystalline anisotropy

Magnetocrystalline anisotropy

Magnetocrystalline anisotropy is the dependence of the internal energy of a ferromagnet on the direction of its magnetization. As a result, certain crystallographic directions are preferred directions, or easy axes, for the magnetization. It is a special case of magnetic anisotropy. The spin-orbit interaction is the primary source of the magnetocrystalline anisotropy.

Magnetocrystalline anisotropy determines whether a magnetic material can be made into a good hard magnet, a good soft magnet or neither. Hard magnets are an essential component of electromagnetic motors and soft magnets are an essential component of transformers.

Contents

Microscopic origin

Magnetocrystalline anisotropy arises mostly from spin-orbit coupling.[1] This effect is weak compared to the exchange interaction and is difficult to compute from first principles, although some successful computations have been made.[2]

Thermodynamic theory

The magnetocrystalline anisotropy energy is generally represented as an expansion in powers of the direction cosines of the magnetization. The magnetization vector can be written M = Ms(α,β,γ), where Ms is the saturation magnetization. Because of time reversal symmetry, only even powers of the cosines are allowed.[3] The nonzero terms in the expansion depend on the crystal system (e.g., cubic or hexagonal).[3] The order of a term in the expansion is the sum of all the exponents of magnetization components, i.e., α β is second order.

Uniaxial anisotropy

A representation of a uniaxial easy axis and easy plane. Arrows represent possible magnetization directions, black for the easy axis and red for the plane.

More than one kind of crystal system has a single axis of high symmetry (threefold, fourfold or sixfold). The anisotropy of such crystals is called uniaxial anisotropy. If the z axis is taken to be the main symmetry axis of the crystal, the lowest order term in the energy is[4]

E/V = K_1 \left(\alpha^2+\beta^2\right) = K_1\left(1-\gamma^2\right). [5]

The ratio E/V is an energy density (energy per unit volume). This can also be represented in spherical polar coordinates with α = cos φ sin θ, β = sin φ sin θ, and γ = cos θ:

\displaystyle E/V = K_1 \sin^2\theta.

The parameter K1, often represented as Ku, has units of energy density and depends on composition and temperature.

The minima in this energy with respect to θ satisfy

\frac{\partial E}{\partial \theta} = 0 \qquad \text{and} \qquad \frac{\partial^2 E}{\partial \theta^2} > 0.

If K1 > 0, the directions of lowest energy are the ± z directions. The z axis is called the easy axis. If K1 < 0, there is an easy plane perpendicular to the symmetry axis (the basal plane of the crystal).

Many models of magnetization represent the anisotropy as uniaxial and ignore higher order terms. However, if K1 < 0, the lowest energy term does not determine the direction of the easy axes within the basal plane. For this, higher-order terms are needed, and these depend on the crystal system (hexagonal, tetragonal or rhombohedral).[3]

Hexagonal system

A representation of an easy cone. All the minimum-energy directions (such as the arrow shown) lie on this cone.

In a hexagonal system the c axis is an axis of sixfold rotation symmetry. The energy density is, to fourth order,

\displaystyle E/V = K_1 \sin^2\theta + K_2 \sin^4\theta + K_3\sin^4\theta\cos 6\phi .

The uniaxial anisotropy is mainly determined by the first two terms. Depending on the values K1 and K2, there are four different cases:[1]

  • When K1 = K2 = 0, the ferromagnet is isotropic.
  • When K1 > 0 and K2 ≥ 0, the c axis is an easy axis.
  • When K1 < 0 and K2 ≤ 0, the basal plane is an easy plane.
  • When K1 and K2 have different signs, the ferromagnet has an easy cone (see figure to right).

The basal plane anisotropy is determined by the third term, which is sixth-order. The easy directions are projected onto three axes in the basal plane.

Below are some room-temperature anisotropy constants for hexagonal ferromagnets. Since all the values of K1 and K2 are positive, these materials have an easy axis.

Room-temperature anisotropy constants ( × 104 J/m3 ). [1]
Structure K1 K2
Co 45 15
αFe2O3 (hematite) 120[6]
BaO· 6Fe2O3 3
YCo5 550
MnBi 89 27

Tetragonal and Rhombohedral systems

The energy density for a tetragonal crystal is[3]

\displaystyle E/V = K_1 \sin^2\theta + K_2 \sin^4\theta + K_3\sin^4\theta \sin 2\phi .

Note that the K3 term, the one that determines the basal plane anisotropy, is fourth order (same as the K2 term). The definition of K3 may vary by a constant multiple between publications.

The energy density for a rhombohedral crystal is[3]

\displaystyle E/V = K_1 \sin^2\theta + K_2 \sin^4\theta + K_3\cos\theta\sin^3\theta \cos 3\phi .

Cubic anisotropy

Energy surface for cubic anisotropy with K1 > 0. Both color saturation and distance from the origin increase with energy. The lowest energy (lightest blue) is arbitrarily set to zero.
Energy surface for cubic anisotropy with K1 < 0. Same conventions as for K1 > 0.

In a cubic crystal the lowest order terms in the energy are[3][1]

 E/V = K_1 \left(\alpha^2\beta^2+\beta^2\gamma^2+\gamma^2\alpha^2\right) + K_2\alpha^2\beta^2\gamma^2.

If the second term can be neglected, the easy axes are the < 100 > axes (i.e., the ± x, ± y, and ± z, directions) for K1 > 0 and the < 111 > directions for K1 < 0 (see images on right).

If K2 is not assumed to be zero, the easy axes depend on both K1 and K2. These are given in the table below, along with hard axes (directions of greatest energy) and intermediate axes (saddle points) in the energy). In energy surfaces like those on the right, the easy axes are analogous to valleys, the hard axes to peaks and the intermediate axes to mountain passes.

Easy axes for K1 > 0. [1]
Type of axis K_2 = +\infty to − 9K1 / 4 K2 = − 9K1 / 4 to − 9K1 K2 = − 9K1 to -\infty
Easy \langle 100 \rangle \langle 100 \rangle \langle 111 \rangle
Medium \langle 110 \rangle \langle 111 \rangle \langle 100 \rangle
Hard \langle 111 \rangle \langle 110 \rangle \langle 110 \rangle
Easy axes for K1 < 0. [1]
Type of axis K_2 = +\infty to − 9K1 / 4 K2 = − 9K1 / 4 to − 9K1 K2 = − 9K1 to -\infty
Easy \langle 111 \rangle \langle 110 \rangle \langle 110 \rangle
Medium \langle 110 \rangle \langle 111 \rangle \langle 100 \rangle
Hard \langle 100 \rangle \langle 100 \rangle \langle 111 \rangle

Below are some room-temperature anisotropy constants for cubic ferromagnets. The compounds involving Fe2O3 are ferrites, an important class of ferromagnets. In general the anisotropy parameters for cubic ferromagnets are higher than those for uniaxial ferromagnets. This is consistent with the fact that the lowest order term in the expression for cubic anisotropy is fourth order, while that for uniaxial anisotropy is second order.

Room-temperature anisotropy constants ( × 104 J/m3 ). [1]
Structure K1 K2
Fe 4.8 \pm 0.5
Ni − 0.5 − 0.2
FeO· Fe2O3 (magnetite) − 1.1
MnO· Fe2O3 − 0.3
NiO· Fe2O3 − 0.62
MgO· Fe2O3 − 0.25
CoO· Fe2O3 − 0.25

Temperature dependence of anisotropy

The magnetocrystalline anisotropy parameters have a strong dependence on temperature. They generally decrease rapidly as the temperature approaches the Curie temperature, so the crystal becomes effectively isotropic.[1] Some materials also have an isotropic point at which K1 = 0. Magnetite (Fe3O4), a mineral of great importance to rock magnetism and paleomagnetism, has an isotropic point at 130 kelvin.[6]

Magnetite also has a phase transition at which the crystal symmetry changes from cubic (above) to monoclinic or possibly triclinic below. The temperature at which this occurs, called the Verwey temperature, is 120 Kelvin.[6]

Magnetostriction

The magnetocrystalline anisotropy parameters are generally defined for ferromagnets that are constrained to remain undeformed as the direction of magnetization changes. However, coupling between the magnetization and the lattice does result in deformation, an effect called magnetostriction. To keep the lattice from deforming, a stress must be applied. If the crystal is not under stress, magnetostriction alters the effective magnetocrystalline anisotropy. If a ferromagnet is single domain (uniformly magnetized), the effect is to change the magnetocrystalline anisotropy parameters.[7]

In practice, the correction is generally not large. In hexagonal crystals, there is no change in K1.[8] In cubic crystals, there is a small change, as in the table below.

Room-temperature anisotropy constants K1 (zero-strain) and K1 (zero-stress) ( × 104 J/m3 ). [8]
Structure K1 K'1
Fe 4.7 4.7
Ni − 6.0 − 5.9
FeO· Fe2O3 (magnetite) − 1.1 − 1.4

Notes

  1. ^ a b c d e f g h Cullity & Graham 2005
  2. ^ Daalderop, Kelly & Schuurmans 1990
  3. ^ a b c d e f Landau, Lifshitz & Pitaevski 2004
  4. ^ An arbitrary constant term is ignored.
  5. ^ The lowest-order term in the energy can be written in more than one way because, by definition, α222 = 1.
  6. ^ a b c Dunlop & Özdemir 1997
  7. ^ Chikazumi 1997, chapter 12
  8. ^ a b Ye, Newell & Merrill 1994

References


Wikimedia Foundation. 2010.

Игры ⚽ Нужно сделать НИР?

Look at other dictionaries:

  • Magnetic anisotropy — is the direction dependence of a material s magnetic properties. In the absence of an applied magnetic field, a magnetically isotropic material has no preferential direction for its magnetic moment while a magnetically anisotropic material will… …   Wikipedia

  • magnet — /mag nit/, n. 1. a body, as a piece of iron or steel, that possesses the property of attracting certain substances, as iron. 2. a lodestone. 3. a thing or person that attracts: The park was a magnet for pickpockets and muggers. [1400 50; late ME… …   Universalium

  • Exchange bias — or exchange anisotropy occurs in bilayers (or multilayers) of magnetic materials where the hard magnetization behavior of an antiferromagnetic thin film causes a shift in the soft magnetization curve of a ferromagnetic film. The exchange bias… …   Wikipedia

  • Anisotropic energy — is energy that is directionally specific. The word Anisotropy means directionally dependent , hence the definition. The most common form of anisotropic energy is Magnetocrystalline Anisotropy, which is commonly studied in ferrimagnets. In… …   Wikipedia

  • Magnetische Anisotropie — beschreibt die Tatsache, dass magnetische Materialien eine Vorzugsrichtung oder Vorzugsebene für die Magnetisierung aufweisen können. Das Maß dafür ist die magnetische Anisotropieenergie, die als die Arbeit definiert ist, die benötigt wird, um… …   Deutsch Wikipedia

  • Magnetic domain — Several grains of NdFeB with magnetic domains made visible via contrast with a Kerr microscope. A magnetic domain describes a region within a magnetic material which has uniform magnetization. This means that the individual magnetic moments of… …   Wikipedia

  • Ferromagnetism — Not to be confused with Ferrimagnetism; for an overview see Magnetism A magnet made of alnico, an iron alloy. Ferromagnetism is the physical theory which explains how materials become magnets. Ferromagnetism is the basic mechanism by which… …   Wikipedia

  • Magnetic hyperthermia — is the name given to an experimental cancer treatment. It is based on the fact that magnetic nanoparticles, when subjected to an alternating magnetic field, produce heat. As a consequence, if magnetic nanoparticles are put inside a tumor and the… …   Wikipedia

  • Domain wall — A domain wall is a term used in physics which can have one of two distinct but similar meanings in magnetism, optics, or string theory. These phenomena can all be generically described as topological solitons which occur whenever a discrete… …   Wikipedia

  • Easy axis — In materials science, the easy axis refers to the energetically favorable direction of the spontaneous magnetization in a ferromagnetic material. This axis is determined by various factors, including the magnetocrystalline anisotropy and the… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”