In metallurgy, stainless steel, also known as inox steel or inox from French "inoxydable", is defined as a steel alloy with a minimum of 10.5[1] or 11% chromium content by mass.[2]

Stainless steel does not stain, corrode, or rust as easily as ordinary steel, but it is not stain-proof.[3] It is also called corrosion-resistant steel or CRES when the alloy type and grade are not detailed, particularly in the aviation industry. There are different grades and surface finishes of stainless steel to suit the environment the alloy must endure. Stainless steel is used where both the properties of steel and resistance to corrosion are required.

Stainless steel differs from carbon steel by the amount of chromium present. Unprotected carbon steel rusts readily when exposed to air and moisture. This iron oxide film (the rust) is active and accelerates corrosion by forming more iron oxide. Stainless steels contain sufficient chromium to form a passive film of chromium oxide, which prevents further surface corrosion and blocks corrosion from spreading into the metal's internal structure.[4]

Passivation only occurs if the proportion of chromium is high enough.

The arch rises from the bottom left of the picture and is shown against a featureless clear sky
The 630-foot (192 m) high, stainless-clad (type 304) Gateway Arch defines St. Louis's skyline.

Contents

History

An announcement, as it appeared in the 1915 New York Times, of the development of stainless steel.[5]

A few corrosion-resistant iron artifacts survive from antiquity. A famous example is the Iron Pillar of Delhi, erected by order of Kumara Gupta I around AD 400. Unlike stainless steel, however, these artifacts owe their durability not to chromium but to their high phosphorus content, which, together with favorable local weather conditions, promotes the formation of a solid protective passivation layer of iron oxides and phosphates, rather than the non-protective cracked rust layer that develops on most ironwork.

The corrosion resistance of iron-chromium alloys was first recognized in 1821 by French metallurgist Pierre Berthier, who noted their resistance against attack by some acids and suggested their use in cutlery. Metallurgists of the 19th century were unable to produce the combination of low carbon and high chromium found in most modern stainless steels, and the high-chromium alloys they could produce were too brittle to be practical.

In the late 1890s Hans Goldschmidt of Germany developed an aluminothermic (thermite) process for producing carbon-free chromium. Between 1904 and 1911 several researchers, particularly Leon Guillet of France, prepared alloys that would today be considered stainless steel.

Friedrich Krupp Germaniawerft built the 366-ton sailing yacht Germania featuring a chrome-nickel steel hull in Germany in 1908.[6] In 1911, Philip Monnartz reported on the relationship between chromium content and corrosion resistance. On October 17, 1912, Krupp engineers Benno Strauss and Eduard Maurer patented austenitic stainless steel as ThyssenKrupp Nirosta.[7]

Similar developments were taking place contemporaneously in the United States, where Christian Dantsizen and Frederick Becket were industrializing ferritic stainless steel. In 1912, Elwood Haynes applied for a US patent on a martensitic stainless steel alloy, which was not granted until 1919.[8]

Also in 1912, Harry Brearley of the Brown-Firth research laboratory in Sheffield, England, while seeking a corrosion-resistant alloy for gun barrels, discovered and subsequently industrialized a martensitic stainless steel alloy. The discovery was announced two years later in a January 1915 newspaper article in The New York Times.[5] The metal was later marketed under the 'Staybrite' brand by Firth Vickers in England and was used for the new entrance canopy for the Savoy Hotel in London in 1929.[9]

Brearley applied for a US patent during 1915 only to find that Haynes had already registered a patent. Brearley and Haynes pooled their funding and with a group of investors formed the American Stainless Steel Corporation, with headquarters in Pittsburgh, Pennsylvania.[10] In the beginning stainless steel was sold in the US under different brand names like 'Allegheny metal' and 'Nirosta steel'. In 1929 before the Great Depression hit, over 25,000 tons of stainless steel was manufactured and sold in the US.[11]

Properties

High oxidation-resistance in air at ambient temperature is normally achieved with additions of a minimum of 13% (by weight) chromium, and up to 26% is used for harsh environments.[12] The chromium forms a passivation layer of chromium(III) oxide (Cr2O3) when exposed to oxygen. The layer is too thin to be visible, and the metal remains lustrous. The layer is impervious to water and air, protecting the metal beneath. Also, this layer quickly reforms when the surface is scratched. This phenomenon is called passivation and is seen in other metals, such as aluminium and titanium. Corrosion-resistance can be adversely affected if the component is used in a non-oxygenated environment, a typical example being underwater keel bolts buried in timber.

When stainless steel parts such as nuts and bolts are forced together, the oxide layer can be scraped off, causing the parts to weld together. When disassembled, the welded material may be torn and pitted, an effect known as galling. This destructive galling can be best avoided by the use of dissimilar materials for the parts forced together, for example bronze and stainless steel, or even different types of stainless steels (martensitic against austenitic), when metal-to-metal wear is a concern. Nitronic alloys reduce the tendency to gall through selective alloying with manganese and nitrogen. In addition, threaded joints may be lubricated to prevent galling.

Applications

The pinnacle of New York's Chrysler Building is clad with type 302 stainless steel.[13]
 A stylized figure of a male human with outstretched arms and head tilted slightly forward, wearing a winged and crested helmet, mounted on the facade of a building
An art deco sculpture on the Niagara-Mohawk Power building in Syracuse, New York.

Stainless steel’s resistance to corrosion and staining, low maintenance and familiar lustre make it an ideal material for many applications. There are over 150 grades of stainless steel, of which fifteen are most commonly used. The alloy is milled into coils, sheets, plates, bars, wire, and tubing to be used in cookware, cutlery, hardware, surgical instruments, major appliances, industrial equipment (for example, in sugar refineries) and as an automotive and aerospace structural alloy and construction material in large buildings. Storage tanks and tankers used to transport orange juice and other food are often made of stainless steel, because of its corrosion resistance and antibacterial properties. This also influences its use in commercial kitchens and food processing plants, as it can be steam-cleaned and sterilized and does not need paint or other surface finishes.

Stainless steel is used for jewellery and watches with 316L being the type commonly used for such applications. It can be re-finished by any jeweler and will not oxidize or turn black.

Some firearms incorporate stainless steel components as an alternative to blued or parkerized steel. Some handgun models, such as the Smith & Wesson Model 60 and the Colt M1911 pistol, can be made entirely from stainless steel. This gives a high-luster finish similar in appearance to nickel plating. Unlike plating, the finish is not subject to flaking, peeling, wear-off from rubbing (as when repeatedly removed from a holster), or rust when scratched.

Some automotive manufacturers use stainless steel as decorative highlights in their vehicles.

Architectural

Stainless steel is used for buildings for both practical and aesthetic reasons. Stainless steel was in vogue during the art deco period. The most famous example of this is the upper portion of the Chrysler Building (pictured). Some diners and fast-food restaurants use large ornamental panels and stainless fixtures and furniture. Because of the durability of the material, many of these buildings retain their original appearance.

The forging of stainless steel has given rise to a fresh approach to architectural blacksmithing in recent years.

Type 316 stainless is used on the exterior of both the Petronas Twin Towers and the Jin Mao Building, two of the world's tallest skyscrapers.[14]

The Parliament House of Australia in Canberra has a stainless steel flagpole weighing over 220 tons (200 metric tonnes).

The aeration building in the Edmonton Composting Facility, the size of 14 hockey rinks, is the largest stainless steel building in North America.

Bridges

  • Minorca Road Bridge (Spain) is the first stainless steel road bridge.
  • Sant Fruitos Pedestrian Bridge (Catalonia, Spain), arch pedestrian bridge.
  • Padre Arrupe Bridge (Bilbao, Spain) links the Guggenheim museum to the University of Deusto.[15]

Monuments and sculptures

  • The Unisphere, constructed as the theme symbol of the 1964-5 World's Fair in New York City, is the world's largest globe-shaped structure.
  • The Gateway Arch (pictured) is clad entirely in stainless steel: 886 tons (804 metric tonnes) of 0.25 in (6.4 mm) plate, #3 finish, type 304 stainless steel.[16]
  • The United States Air Force Memorial has an austenitic stainless steel structural skin.
  • The Atomium in Brussels, Belgium was renovated with stainless-steel cladding in a renovation completed in 2006; previously the spheres and tubes of the structure were clad in aluminium.
  • The Cloud Gate sculpture by Anish Kapoor, in Chicago US.
  • The Sibelius monument in Helsinki, Finland, is made entirely of stainless steel tubes.

Other

Recycling and reuse

Stainless steel is 100% recyclable. An average stainless steel object is composed of about 60% recycled material of which approximately 40% originates from end-of-life products and about 60% comes from manufacturing processes.[17] According to the International Resource Panel's Metal Stocks in Society report, the per capita stock of stainless steel in use in society is 80–180kg in more developed countries and 15kg in less-developed countries.

There is a secondary market that recycles usable scrap for many stainless steel markets. The product is mostly coil, sheet and blanks. This material is purchased at a less-than-prime price and sold to commercial quality stampers and sheet metal houses. The material may have scratches, pits and dents but is made to the current specifications.

Types of stainless steel

Several heavy pieces of bent pipe with flange connections, strapped down to a wooden pallet
Pipes and fittings made of stainless steel.

There are different types of stainless steels: when nickel is added, for instance, the austenite structure of iron is stabilized. This crystal structure makes such steels virtually non-magnetic and less brittle at low temperatures. For greater hardness and strength, more carbon is added. With proper heat treatment, these steels are used for such things as razor blades, cutlery, and tools.

Significant quantities of manganese have been used in many stainless steel compositions. Manganese preserves an austenitic structure in the steel as does nickel, but at a lower cost.

Stainless steels are also classified by their crystalline structure:

  • Austenitic, or 300 series, stainless steels make up over 70% of total stainless steel production. They contain a maximum of 0.15% carbon, a minimum of 16% chromium and sufficient nickel and/or manganese to retain an austenitic structure at all temperatures from the cryogenic region to the melting point of the alloy. A typical composition of 18% chromium and 10% nickel, commonly known as 18/10 stainless, is often used in flatware. 18/0 and 18/8 are also available. Superaustenitic stainless steels, such as alloy AL-6XN and 254SMO, exhibit great resistance to chloride pitting and crevice corrosion because of high molybdenum content (>6%) and nitrogen additions, and the higher nickel content ensures better resistance to stress-corrosion cracking versus the 300 series. The higher alloy content of superaustenitic steels makes them more expensive. Other steels can offer similar performance at lower cost and are preferred in certain applications.[citation needed] Low-carbon versions, for example 316L or 304L, are used to avoid corrosion problems caused by welding. Grade 316LVM is preferred where biocompatibility is required (such as body implants and piercings).[18] The "L" means that the carbon content of the alloy is below 0.03%, which reduces the sensitization effect (precipitation of chromium carbides at grain boundaries) caused by the high temperatures involved in welding.
  • Ferritic stainless steels generally have better engineering properties than austenitic grades, but have reduced corrosion resistance, because of the lower chromium and nickel content. They are also usually less expensive. They contain between 10.5% and 27% chromium and very little nickel, if any, but some types can contain lead. Most compositions include molybdenum; some, aluminium or titanium. Common ferritic grades include 18Cr-2Mo, 26Cr-1Mo, 29Cr-4Mo, and 29Cr-4Mo-2Ni. These alloys can be degraded by the presence of σ chromium, an intermetallic phase which can precipitate upon welding.
  • Martensitic stainless steels are not as corrosion-resistant as the other two classes but are extremely strong and tough, as well as highly machinable, and can be hardened by heat treatment. Martensitic stainless steel contains chromium (12–14%), molybdenum (0.2–1%), nickel (less than 2%), and carbon (about 0.1–1%) (giving it more hardness but making the material a bit more brittle). It is quenched and magnetic.
  • Precipitation-hardening martensitic stainless steels have corrosion resistance comparable to austenitic varieties, but can be precipitation hardened to even higher strengths than the other martensitic grades. The most common, 17-4PH, uses about 17% chromium and 4% nickel. The Lockheed-Martin Joint Strike Fighter is the first aircraft to use a precipitation-hardenable stainless steel—Carpenter Custom 465—in its airframe.
  • Duplex stainless steels have a mixed microstructure of austenite and ferrite, the aim usually being to produce a 50/50 mix, although in commercial alloys the ratio may be 40/60. Duplex stainless steels have roughly twice the strength compared to austenitic stainless steels and also improved resistance to localized corrosion, particularly pitting, crevice corrosion and stress corrosion cracking. They are characterized by high chromium (19–32%) and molybdenum (up to 5%) and lower nickel contents than austenitic stainless steels. Duplex grades are characterized into groups based on their alloy content and corrosion resistance. Lean duplex refers to grades such as UNS S32101 (LDX 2101), S32304, and S32003. The standard duplex is 22% chromium with UNS S31803/S32205 known as 2205 being the most widely used. Super duplex is by definition a duplex stainless steel with a pitting corrosion equivalent (PRE) > 40, where PRE = %Cr + 3.3x(%Mo + 0.5x%W) + 16x%N. Usually super duplex grades have 25% chromium or more and some common examples are S32760 (Zeron 100), S32750 (2507) and S32550 (Ferralium), although not all Ferralium grades are super duplex grades. Hyper duplex refers to duplex grades with a PRE > 48 and at the moment only UNS S32707 and S33207 are available on the market. The properties of duplex stainless steels are achieved with an overall lower alloy content than similar-performing super-austenitic grades, making their use cost-effective for many applications.

Comparison of standardized steels

EN-standard

Steel no. k.h.s DIN

EN-standard

Steel name

SAE grade UNS
440A S44002
1.4112 X90CrMoV18 440B S44003
1.4125 440C S44004
440F S44020
1.4016 X6Cr17 430 S43000
1.4408 G-X 6 CrNiMo 18-10 316
1.4512 X6CrTi12 409 S40900
410 S41000
1.4310 X10CrNi18-8 301 S30100
1.4318 X2CrNiN18-7 301LN N/A
1.4307 X2CrNi18-9 304L S30403
1.4306 X2CrNi19-11 304L S30403
1.4311 X2CrNiN18-10 304LN S30453
1.4301 X5CrNi18-10 304 S30400
1.4948 X6CrNi18-11 304H S30409
1.4303 X5CrNi18-12 305 S30500
X5CrNi30-9 312
1.4541 X6CrNiTi18-10 321 S32100
1.4878 X12CrNiTi18-9 321H S32109
1.4404 X2CrNiMo17-12-2 316L S31603
1.4401 X5CrNiMo17-12-2 316 S31600
1.4406 X2CrNiMoN17-12-2 316LN S31653
1.4432 X2CrNiMo17-12-3 316L S31603
1.4435 X2CrNiMo18-14-3 316L S31603
1.4436 X3CrNiMo17-13-3 316 S31600
1.4571 X6CrNiMoTi17-12-2 316Ti S31635
1.4429 X2CrNiMoN17-13-3 316LN S31653
1.4438 X2CrNiMo18-15-4 317L S31703
1.4362 X2CrNi23-4 2304 S32304
1.4462 X2CrNiMoN22-5-3 2205 S31803/S32205
1.4539 X1NiCrMoCu25-20-5 904L N08904
1.4529 X1NiCrMoCuN25-20-7 1925hMo/6MO N08926
1.4547 X1CrNiMoCuN20-18-7 254SMO S31254

Stainless steel grades

There are a number of different systems for grading stainless and other steels. The article on US SAE steel grades details a large number of grades with their properties.

Stainless steel in 3D printing

Some 3D printing providers have developed proprietary stainless steel sintering[19] blends for use in rapid prototyping. Currently available grades do not vary significantly in their properties.[20]

Stainless steel finishes

Matte surface of pipe, with a few horizontal scratches
316L stainless steel, with an unpolished, mill finish.

Standard mill finishes can be applied to flat rolled stainless steel directly by the rollers and by mechanical abrasives. Steel is first rolled to size and thickness and then annealed to change the properties of the final material. Any oxidation that forms on the surface (mill scale) is removed by pickling, and a passivation layer is created on the surface. A final finish can then be applied to achieve the desired aesthetic appearance.

  • No. 0: Hot rolled, annealed, thicker plates
  • No. 1: Hot rolled, annealed and passivated
  • No. 2D: Cold rolled, annealed, pickled and passivated
  • No. 2B: Same as above with additional pass-through highly polished rollers
  • No. 2BA: Bright annealed (BA or 2R) same as above then bright annealed under oxygen-free atmospheric condition
  • No. 3: Coarse abrasive finish applied mechanically
  • No. 4: Brushed finish
  • No. 5: Satin finish
  • No. 6: Matte finish
  • No. 7: Reflective finish
  • No. 8: Mirror finish
  • No. 9: Bead blast finish
  • No. 10: Heat colored finish-wide range of electropolished and heat colored surfaces

See also

References

  1. ^ "The Stainless Steel Family". http://www.worldstainless.org/NR/rdonlyres/B2617D50-73AE-4FAB-BDCD-88ABD7891B97/4933/TheStainlessSteelFamily.pdf. Retrieved 2009-11-12. 
  2. ^ "Steel Glossary". American Iron and Steel Institute (AISI). http://www.steel.org/AM/Template.cfm?Section=Steel_Glossary2&CONTENTID=6426&TEMPLATE=/CM/HTMLDisplay.cfm. Retrieved October 21, 2008. 
  3. ^ "Why is Stainless Steel Stainless?". http://www.stainless-online.com/why-stainless-steel-stainless.htm. Retrieved 2008-12-20. .
  4. ^ Stainless Steels and Alloys: Why They Resist Corrosion and How They Fail"
  5. ^ a b "A non-rusting steel". New York Times. 31 January 1915. 
  6. ^ "A Proposal to Establish the Shipwreck Half Moon as a State Underwater Archaeological Preserve". Bureau of Archaeological Research, Division of Historical Resources, Florida Department of State. May 2000. http://dhr.dos.state.fl.us/archaeology/underwater/preserves/HM_Prop3.pdf. 
  7. ^ "ThyssenKrupp Nirosta: History". http://www.nirosta.de/History.22.0.html?&L=1. Retrieved 2007-08-13. 
  8. ^ Scientific American Inventions and Discoveries, p. 380, Rodney P. Carlisle, John Wiley and Sons, 2004, ISBN 0471244104, ISBN 9780471244103
  9. ^ Sheffield Steel, ISBN 0-7509-2856-5
  10. ^ Cobb, Harold M. (2010). The History of Stainless Steel. ASM Internationa. p. 360. ISBN 1615030107. 
  11. ^ "New Steel Alloy Is Rust Proof", December 1930, Popular Science
  12. ^ Ashby, Michael F.; & David R. H. Jones (1992) [1986]. "Chapter 12". Engineering Materials 2 (with corrections ed.). Oxford: Pergamon Press. pp. 119. ISBN 0-08-032532-7. 
  13. ^ "What is Stainless Steel?". Nickel Institute. http://www.nickelinstitute.org/index.cfm/ci_id/11021.htm. Retrieved 2007-08-13. 
  14. ^ What is Stainless Steel?
  15. ^ "Stainless Steel Bridge in Bilbao". Outokumpu. http://www.outokumpu.com/Industry-offerings/Architecture-Building-and-Construction/Case-Studies-Container/Bilbao-bridge/. 
  16. ^ Gateway Arch Fact Sheet
  17. ^ "The Recycling of Stainless Steel ("Recycled Content" and "Input Composition" slides)" (Flash). International Stainless Steel Forum. 2006. http://www.worldstainless.org/ISSF/Files/Recycling08/Flash.html. Retrieved 2006-11-19. 
  18. ^ Material Properties Data: Marine Grade Stainless Steel
  19. ^ Shapeways: Stainless Steel
  20. ^ Material Properties Data: 3D Printing Steel

External links


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • stainless steel — n [U] a type of steel that does not ↑rust ▪ stainless steel cutlery …   Dictionary of contemporary English

  • stainless steel — noun uncount steel that has been treated to stop RUST from forming on its surface, used for making knives, tools, and other things ╾ ,stainless steel adjective …   Usage of the words and phrases in modern English

  • stainless-steel — adjective Thesaurus: made of a particular metalhyponym types of metalhypernym Main entry: stainless steel …   Useful english dictionary

  • stainless steel — 1917, a chromium steel alloy (usually 14% chromium) used for cutlery, etc., so called because it is highly resistant to rust or tarnish …   Etymology dictionary

  • stainless steel — ► NOUN ▪ a form of steel containing chromium, resistant to tarnishing and rust …   English terms dictionary

  • stainless steel — n. steel alloyed with chromium, etc., virtually immune to rust and corrosion …   English World dictionary

  • Stainless steel — Stainless steel. См. Нержавеющая сталь. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • Stainless Steel — Rohrleitungsteile und Formstücke aus rostfreiem Stahl Rostfreier Stahl ist ein allgemeinsprachlicher Ausdruck für eine Gruppe von korrosions und säurebeständigen Stahlsorten. Diese Stähle sind auch bekannt unter der korrekteren Bezeichnung… …   Deutsch Wikipedia

  • Stainless Steel — Stain|less Steel 〈[ stɛınlɛs sti:l] engl. Bez. für〉 rostfreier Stahl * * * Stainless Steel   [ steɪnles stiːl, englisch] der, , nicht rostender Stahl, Qualitätsbezeichnung auf Gebrauchsgütern. * * * Stain|less Steel [ steɪnlɪs sti:l], der; [engl …   Universal-Lexikon

  • stainless steel — [[t]ste͟ɪnləs sti͟ːl[/t]] N UNCOUNT Stainless steel is a metal made from steel and chromium which does not rust. ...a stainless steel sink …   English dictionary

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”